Resumo: A resistência de união de pinos à dentina radicular pode ser comprometida ao longo do tempo pela degradação da interface adesiva. Por isso, o objetivo deste estudo foi avaliar o efeito do pré-tratamento da dentina radicular com clorexidina 2% (CHX), etanol 100% (EtOH) e hipoclorito de sódio 5,25% (NaOCl) e a associação dessas substâncias, na resistência de união e durabilidade adesiva de pinos de fibra de vidro reembasados com resina composta à dentina radicular. Também foram avaliadas a técnica úmida (TU) e seca (TS) (secagem com jatos de ar por 5 segundos). No capítulo 1 que compõe este trabalho, os prétratamentos foram: G1(controle)- irrigação com soro fisiológico; G2- TS; G3- CHX por 5 minutos; G4- EtOH por 1 minuto; e G5- CHX por 5 minutos seguido de EtOH por 1 minuto. Logo após, os canais foram secos com cones de papel absorvente (TU) e a dentina hibridizada com Scotch Bond. No G2, após a TU foi realizada TS. Pinos fibra de vidro reembasados com resina composta foram cimentados com Rely X ARC. Cada grupo foi dividido em 3 subgrupos: 24 horas de armazenamento em água; 12 meses em água; 12 meses em óleo. Todos as raízes foram seccionadas, o teste de push-out realizado e os valores de resistência de união analisados estatisticamente pelos testes ANOVA/Tukey's (a=0,05). Os grupos imediatos apresentaram valores similares (P>0,05), com exceção da TS que resultou em menores valores de resistência de união (P<0,05).
A CHX preservou os valores nos grupos estocados por 12 meses (P>0,05), e os demais grupos estocados apresentaram redução nos valores de resistência de união (P<0,05). Pode-se concluir que apenas a CHX foi capaz de preservar os valores de resistência por 12 meses. No capítulo 2, foi realizado o pré-tratamento da dentina radicular com NaOCl isolado e em associação com CHX e/ou EtOH, além da realização da TU e TS. O sistema adesivo, os demais procedimentos e análise estatística foram similares ao capítulo 1. Os resultados mostraram maiores
valores de resistência de união nos grupos onde apenas o NaOCl foi utilizado ou associado à CHX, com a TU ou TS, nos grupos imediatos e armazenados por 12 meses (P>0.05). Nos grupos onde EtOH foi utilizado, os valores de resistência de união foram menores (P<0,05). Foi possível concluir que o NaOCl isolado ou associdado com CHX foi capaz de preservar os valores de resistência de união por 12 meses. No capítulo 3, os grupos foram iguais aos do capítulo 1, no entanto a TS não foi estudada e o adesivo utilizado foi o Clearfil SE Bond. O preparo das amostras e análise estatística foram similares ao capítulo 1. Os grupos imediatos apresentaram valores similares de resistência de união (P>0,05). Houve diminuição significante nos grupos controles após 12 meses de armazenamento (P<0,05). O uso de CHX e/ou EtOH preservou os valores de resistência de união por 12 meses (P>0,05). Pode-se concluir que o pré-tratamento da dentina com CHX e/ou EtOH foi capaz de preservar a resistência de união por 12 meses.
Ver menos

Abstract: The bond strength of posts to root dentin can be compromised over time by adhesive interface degradation. Therefore, the aim of this study was to investigate the effects of pre-treatment of root dentin with 2% chlorhexidine (CHX), 100% ethanol (EtOH) and 5.25% sodium hypochlorite (NaOCl), as well as the association of these substances, on the bond strength and adhesive durability of fiber posts relined with resin composite to root dentin. The wet (WT) and dry (ST) (air-drying for five seconds) techniques were also evaluated. The first chapter of this work, the pre-treatments were: G1-control, irrigation with physiologic solution; G2, ST; G3, 5 minutes with CHX; G4, 1 minute with EtOH; and G5, 5 minutes with CHX followed by 1 minute EtOH. Afterwards, the root canals were dried with absorbent paper cones (WT) and the dentin hybridized with Scotch Bond. In G2, after WT was realized ST. Fiber post relining with resin composite was cemented with RelyX ARC. Each group was randomly divided into three subgroups: 24 h of water storage, 12 months of water storage, and 12 months of oil storage. All roots were sectioned transversely, the push-out test was performed and bond strength values were analyzed by ANOVA/Tukey's test (a=0.05). Immediate groups showed
similars bond strengths (P>0.05), except that the ST significantly decreased bond strength (P<0.05). The use of CHX preserved bond strength in the groups stored in
water and oil for 12 months (P>0.05). The other groups stored for 12 months showed a significant decrease in bond strength (P<0.05). It may be concluded that
CHX preserved the bond strength for 12 months. In the second chapter, pretreatment of root dentin was performed with NaOCl alone, and associated with CHX and/or EtOH. In addition ST and WT were performed. The adhesive system, the sample preparation and statistical analysis were similar to those used in the first chapter. The results showed that the groups in which NaOCl was used alone or associated with CHX showed the highest bond strength values with ST or WT in
the immediate and groups stored for 12 months (P>0.05). The groups that used EtOH showed lower bond strength and there was a statistical similarity between them (P<0.05). It may be concluded that the use of NaOCl or NaOCl associated with CHX preserved the bond strength to root dentin for 12 months. In the third chapter, the treatments were the same as those in the first chapter. However, the ST was not studied and the adhesive used was Clearil SE Bond. The sample preparation and statistical analysis were similar to those used in the first chapter. Immediate groups showed similar bond strength values with or without CHX and/or
EtOH pre-treatment (P>0.05). A significant decrease in the bond strength was observed in the control groups after 12 months of storage in water and oil (P<0.05). It may be concluded that the use of CHX and/or EtOH preserved bond strength in the groups stored in water and oil for 12 months (P<0.05).
Ver menos