Caracteristicas da usinagem de um composito de resina fenolica reforçada com fibras de vidro e carbono
João Roberto Ferreira
DISSERTAÇÃO
Português
T/UNICAMP F414c
Campinas, SP : [s.n.], 1992.
[156]f. : il.
Orientador: Nivaldo Lemos Cupini
Dissertação (mestrado) - Universidade estadual de Campinas, Faculdade de Engenharia Mecanica
Resumo: Este trabalho consiste na realização de experimentos para analisar o comportamento de ferramentas de diversos materiais no torneamento de compósitos de resina fenólica reforçada com fibras de vidro e carbono, moldadas nas formas de laminados e bobinados. As ferramentas utilizadas foram:...
Ver mais
Resumo: Este trabalho consiste na realização de experimentos para analisar o comportamento de ferramentas de diversos materiais no torneamento de compósitos de resina fenólica reforçada com fibras de vidro e carbono, moldadas nas formas de laminados e bobinados. As ferramentas utilizadas foram: cerâmica pura (A1203+Zr02) , cerâmica mista (Al203+TiC) , SIALON (Al203+Si3N4) , cerâmica reforçada com whiskers (Al203+SiC), metal duro ISO Kl0, nitreto de boro cúbico (CBN) , e diamante (PCD). Durante os ensaios foram observados os desgastes das ferramentas, a rugosidade superficial da peça, e a força de avanço, em função do comprimento (tempo) de corte, da velocidade de corte, e da orientação das fibras no compósito. Uma das mais importantes conclusões deste trabalho é que a rugosidade superficial do compósito aumenta de maneira progressiva com o desgaste da ferramenta, viabilizando somente o emprego da ferramenta de diamante em torneamento de acabamento. Em operação de desbaste o metal duro apresenta-se como a melhor solução, pois apesar de sofrer desgaste superior ao diamante é mais barato e dispensa cuidados operacionais especiais
Ver menos
Abstract: Some experiments were carried out to study the performance of many different tool materials, like pure ceramic (AI203+Zr02), mixed ceramic (A1203+TiC) , SIALON (A1203+SbN4) , whiskers reinforced ceramic (AI203+sic) , cemented carbide ISO K10, cubic boron nitride (CBN), o and diamond (PCD)....
Ver mais
Abstract: Some experiments were carried out to study the performance of many different tool materials, like pure ceramic (AI203+Zr02), mixed ceramic (A1203+TiC) , SIALON (A1203+SbN4) , whiskers reinforced ceramic (AI203+sic) , cemented carbide ISO K10, cubic boron nitride (CBN), o and diamond (PCD). They were tested in turning of carbon and glass fiber reinforced fenolic resin
composite. Two different workpiece shapes were used, laminated plate and filament wound tube. During the experiments, tool wear,
surface roughness, and machining forces behaviour were observed, under several cutting lengths (or cutting times), cutting speeds,
and fiber directions in the composite. The experimental results showed that, due to the great influence of tool wear in workpiece
surface roughness, only diamond tools are technically suitable to be used in finish turning. In rough turning, the cemented carbide
tools proved to be the best solution. Al though, it presented larger wear than diamond, the relationship cost and benefit showed
to be much lower and, besides, it is not necessary special operational care Ver menos
composite. Two different workpiece shapes were used, laminated plate and filament wound tube. During the experiments, tool wear,
surface roughness, and machining forces behaviour were observed, under several cutting lengths (or cutting times), cutting speeds,
and fiber directions in the composite. The experimental results showed that, due to the great influence of tool wear in workpiece
surface roughness, only diamond tools are technically suitable to be used in finish turning. In rough turning, the cemented carbide
tools proved to be the best solution. Al though, it presented larger wear than diamond, the relationship cost and benefit showed
to be much lower and, besides, it is not necessary special operational care Ver menos
Caracteristicas da usinagem de um composito de resina fenolica reforçada com fibras de vidro e carbono
João Roberto Ferreira
Caracteristicas da usinagem de um composito de resina fenolica reforçada com fibras de vidro e carbono
João Roberto Ferreira