Blendas com poli(3-hidroxibutirato) (PHB) e copolimeros aleatorios = comportamento de fases e cinetica de cristalização
Eduardo dos Santos Tada
TESE
Português
T/UNICAMP T12b
[Blends of poly(3-hydroxybutyrate) and random copolymers]
Campinas, SP : [s.n.], 2009.
224 p. : il.
Orientador: Maria Isabel Felisberti
Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica
Resumo: Blendas do polímero biodegradável poli(hidroxibutirato) foram preparadas com os seguintes copolímeros aleatórios: poli(estireno-co-acrilonitrila)-SAN; poli(estireno-co-metacrilato de 2-hidróxietila)-S-Hema; poli(metacrilato de metila-co-vinil fenol-P(MMA-co-VPh). Os copolímeros SAN foram...
Ver mais
Resumo: Blendas do polímero biodegradável poli(hidroxibutirato) foram preparadas com os seguintes copolímeros aleatórios: poli(estireno-co-acrilonitrila)-SAN; poli(estireno-co-metacrilato de 2-hidróxietila)-S-Hema; poli(metacrilato de metila-co-vinil fenol-P(MMA-co-VPh). Os copolímeros SAN foram sintetizados via copolimerização em massa, enquanto os copolímeros S-Hema foram sintetizados pela copolimerização em solução utilizando DMF como solvente. Os copolímeros foram caracterizados por ressonância magnética nuclear (RMN) de H e C, cromatografia de permeação em gel (GPC), calorimetria exploratória diferencial (DSC) e análise dinâmico-mecânica (DMA). As blendas foram preparadas dissolvendo-se os polímeros em um bom solvente e adicionando-se à solução resultante um mau solvente para a coagulação dessas blendas. As análises das blendas por DSC, DMA e microscopia eletrônica de varredura (SEM) mostraram que todas elas são imiscíveis. A cinética de cristalização do PHB em blendas P(MMA-co-VPh)/PHB e SAN/PHB foi estudada por DSC. Esses estudos mostraram que a presença do copolímero P(MMA-co-VPh) causa a diminuição da taxa de cristalização do PHB e aumenta a energia de ativação do processo de cristalização do PHB. Para as blendas PHB/SAN, o efeito do copolímero em diminuir a taxa de cristalização do PHB é menor que nas blendas PHB/P(MMAco- VPh). Além disso, o teor de acrilonitrila no copolímero pouco afeta a taxa de cristalização do PHB. Os expoentes de Avrami ¿n¿ determinados para a cristalização do PHB nas blendas P(MMA-co-VPh)/PHB e SAN/PHB são aproximadamente iguais ao expoente ¿n¿ para o PHB puro indicando que o mecanismo de cristalização do PHB não se altera nas blendas. Sendo assim, este trabalho possibilitou o entendimento de aspectos importantes referentes ao comportamento de fases e à cinética de cristalização de blendas contendo PHB associado a copolímeros aleatórios.Os estudos cinéticos podem colaborar para a compreensão do comportamento de cristalização de copolímeros/PHB em equipamentos de processamento. Além disso, esse estudo pode ajudar na escolha do copolímero e de sua composição para um melhor controle da cristalização do PHB nessas blendas
Ver menos
Abstract: Blends of biodegradable poly(hydroxybutyrate) were prepared with the following random copolymers: poly(styrene-co-acrylonitrile)-SAN; poly(styrene-co-2-hydroxyethylmethacrilate)-S-Hema; poly(methylmethacrylateco- vinylphenol)-P(MMA-co-VPh).SAN copolymers were synthesized by bulk...
Ver mais
Abstract: Blends of biodegradable poly(hydroxybutyrate) were prepared with the following random copolymers: poly(styrene-co-acrylonitrile)-SAN; poly(styrene-co-2-hydroxyethylmethacrilate)-S-Hema; poly(methylmethacrylateco- vinylphenol)-P(MMA-co-VPh).SAN copolymers were synthesized by bulk copolymerization; while S-Hema copolymers were synthesized by solution copolymerization using DMF as solvent. The resulting copolymers were characterized by nuclear magnetic resonance (RMN) of H and C, gel permeation chromatography (GPC), differential scanning calorimetry (DSC) and dynamic-mechanical analysis (DMA). Blends were prepared using coprecipitation method where a binary homogeneous soilution was added to a large volume of non solvent. DSC, DMA and scanning electron microscopy (SEM) analysis revealed that all the blends are immiscible in the entire composition range. Despite the immiscible blends, DSC analysis show that the copolymers interferes in the PHB crystallization, being capable of suppress this process in some blends. Crystallization kinetics of the PHB in PHB/P(MMA-co-VPh) and PHB/SAN blends was studied by DSC and the results revealed that the presence of P(MMA-co-VPh) copolymer decreases the PHB crystallization rate and increases the activation energy for the overall crystallization process. In respect to PHB/SAN blends, the influence of the copolymer in decrease the PHB crystallization rate is lower than the observed in PHB/P(MMA-co-VPh) blends. Moreover, the acrylonitrile concentration in the copolymer causes little effect in the PHB crystallization rate. The Avrami exponent ¿n¿ determined for the crystallization process in PHB/P(MMA-co-VPh) and SAN/PHB blends are approximately equal to the ¿n¿ exponent for pure PHB indicating that the crystallization mechanisms for pure PHB do not change in the blends. This work made possible the understanding of important aspects of the phase behavior and crystallization kinetics of random copolymers/PHB blends. The crystallization kinetics studies can collaborate for the understanding of the behavior of crystallization of these blends in processing equipments. Moreover, this study can help in the choice of the copolymer and its composition for better control of the crystallization of PHB in these blends
Ver menos
Felisberti, Maria Isabel, 1959-
Orientador
Silva, Maria Elisa Sacarpelli Ribeiro e
Avaliador
Duek, Eliana Aparecida de Rezende, 1961-
Avaliador
De Paoli, Marco-Aurelio, 1949-
Avaliador
Gonçalves, Maria do Carmo, 1957-
Avaliador
Blendas com poli(3-hidroxibutirato) (PHB) e copolimeros aleatorios = comportamento de fases e cinetica de cristalização
Eduardo dos Santos Tada
Blendas com poli(3-hidroxibutirato) (PHB) e copolimeros aleatorios = comportamento de fases e cinetica de cristalização
Eduardo dos Santos Tada
Exemplares
Nº de exemplares: 1
Não existem reservas para esta obra