Avaliação do desempenho de filmes contendo silanos e sais de terras raras para proteção contra corrosão de camadas de ZnFe eletrodepositadas
Marcia Cristina Gonçalves dos Santos
TESE
Português
T/UNICAMP Sa59a
[Evaluation of the performance of films containing silanes and rare earth salts for protection of zinc-iron alloy electroplated against corrosion]
Campinas, SP : [s.n.], 2009.
121 p. : il.
Orientador: Celia Marina de Alvarenga Freire
Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica
Resumo: Aço galvanizado e aço eletrodepositado com liga ZnFe são materiais comuns na indústria de construção civil e automotiva. Esses materiais à base de zinco necessitam, entretanto, serem protegidos de ambientes corrosivos através de um tratamento de superfície que geralmente contém cromo...
Ver mais
Resumo: Aço galvanizado e aço eletrodepositado com liga ZnFe são materiais comuns na indústria de construção civil e automotiva. Esses materiais à base de zinco necessitam, entretanto, serem protegidos de ambientes corrosivos através de um tratamento de superfície que geralmente contém cromo hexavalente ( Cr6+), tóxico para o meio ambiente e cancerígeno para o homem. O presente trabalho apresenta um estudo com filmes contendo diferentes silanos: viniltrietoxissilano (VS), bis-(1,2-[trietoxissilil] etano) (BTSE) ou bis-(3-[trietoxissilil]-propil? tetrassulfeto (BTESPTS) e nitratos de terras raras (Ce ou La), como revestimentos de conversão para a camada de liga ZnFe. Esses sistemas foram avaliados através das análises de Espectroscopia Fotoelétrica de Emissão de Raios-X (XPS), das Curvas de Polarização, da Espectroscopia de Impedância Eletroquímica (EIE), da Microscopia Eletrônica de Varredura (MEV) e Espectrometria de Energia Dispersiva (EDS). Os resultados de EIE e polarização indicaram que os sistemas estudados foram eficientes contra corrosão e que seu desempenho dependia do tipo de silano. Os sistemas ZnFe+Ce+BTSE+BTESPTS e ZnFe+La+BTSE+BTESPTS mostraram o melhor resultado contra corrosão.
Ver menos
Abstract: Galvanized and zinc electroplated steels are very useful materials in automotive and construction industries. These zinc based materials, however, need to be protected against corrosive environments through a surface treatment that generally has hexavalent chromium wich is toxic to the...
Ver mais
Abstract: Galvanized and zinc electroplated steels are very useful materials in automotive and construction industries. These zinc based materials, however, need to be protected against corrosive environments through a surface treatment that generally has hexavalent chromium wich is toxic to the environment and may cause cancer to human being. This thesis shows a study about films containing different silanes: vinyltriethoxysilane (VS), bis-(1,2-[triethoxysilyl]ethane) (BTSE) or is-(3-[triethoxysilyl]-propyl]tetrasulfide (BTESPTS) and rare earth nitrates (Ce, La) as conversion coatings to the zinc-iron alloy electroplated steel. These systems were evaluated using X-Ray Photoelectron Spectroscopy (XPS), Polarization Curves, Electrochemical Impedance Spectroscopy (EIS), Scanning Electron Microscopy (SEM) and EDS. The EIS and Polarization results have shown that the systems under study were efficient against corrosion and its performance depended upon the type of silane. The inciron+Ce+BTSE+ BTESPT and zinc-iron+La+BTSE+BTESPT systems have shown the best result against corrosion.
Ver menos
Freire, Celia Marina de Alvarenga, 1960-
Orientador
Aoki, Idalina Vieira
Avaliador
Pessine, Elisabete Jorge
Avaliador
Duek, Eliana Aparecida de Rezende, 1961-
Avaliador
Ierardi, Maria Clara Filippini, 1951-
Avaliador
Avaliação do desempenho de filmes contendo silanos e sais de terras raras para proteção contra corrosão de camadas de ZnFe eletrodepositadas
Marcia Cristina Gonçalves dos Santos
Avaliação do desempenho de filmes contendo silanos e sais de terras raras para proteção contra corrosão de camadas de ZnFe eletrodepositadas
Marcia Cristina Gonçalves dos Santos
Exemplares
Nº de exemplares: 2
Não existem reservas para esta obra