Efeito da proporção entre pastas base e catalisadora do cimento resinoso e da forma de pinos pre-fabricados na resistencia a tração
Monica da Consolação Canuto Salgueiro
DISSERTAÇÃO
Português
(Broch.)
T/UNICAMP Sa32e
[Effect of the ratio between folders base and catalytic of the resinous cement and the form of bolts daily pay-manufactured in the tensile strenght]
Campinas, SP : [s.n.], 2005.
43 f. : il.
Orientador: Luis Alexandre Maffei Sartini Paulillo
Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Resumo: O objetivo deste trabalho foi avaliar a resistência à tração de pinos intra-radiculares estéticos, com diferentes formas, fixados com cimento resinoso dual com diferentes proporções de catalisador em relação a base. Foram utilizados 60 incisivos bovinos com dimensões semelhantes. A coroa foi...
Ver mais
Resumo: O objetivo deste trabalho foi avaliar a resistência à tração de pinos intra-radiculares estéticos, com diferentes formas, fixados com cimento resinoso dual com diferentes proporções de catalisador em relação a base. Foram utilizados 60 incisivos bovinos com dimensões semelhantes. A coroa foi separada da raiz através de um disco diamantado dupla face no comprimento de 16 mm a partir do ápice. Em seguida, todos os canais radiculares foram obturados e as raízes receberam uma marca a 2,0 mm simulando o limite amelo-cementário e uma camada de resina composta foi inserida na região apical da raiz para aumentar a retenção da mesma no bloco de resina de poliestireno durante o ensaio mecânico. As amostras foram distribuídas, aleatoriamente,em seis grupos experimentais (n=10), sendo que em 30 raízes foram fixados os pinos cônico liso e nas outras 30 raízes os pinos paralelo serrilhado.Para a cimentação dos pinos, as raízes foram desobturadas em 12mm com broca Gates Gliden n° 3 e para o preparo do canal foi usada a broca específica para cada pino. Em seguida, os pinos foram fixados aplicando-se o sistema adesivo Single Bond (3M) e o cimento resinoso dual Rely X (3M) com diferentes proporções de base/catalisador (b/c):G1 - pinos paralelo serrilhado cimentados na proporção 1:1, G2 - pinos paralelo serrilhado cimentados na proporção 1:2, G3 - pinos paralelo serrilhado cimentados na proporção 1:3, G4 - pinos cônico liso cimentados na proporção 1:1, G5 ¿ pinos cônico liso cimentados na proporção 1:2,G6- pinos cônico liso cimentados na proporção 1:3. Após armazenagem por uma semana em estufa a 37°C, as amostras foram submeti.das ao ensaio de resistência à tração numa Instron a velocidade de 1mm/mim, até o deslocamento do pino. Os dados foram submetidos à análise de variância que evidenciou diferença estatística significativa para os fatores Pinos e Proporção, não havendo diferença estatística para a interação pino x proporção. Para melhor evidenciar esse resultado foi aplicado para cada fator o teste de Variação Múltipla de Tukey (LSMEANS) que mostrou que quando se triplicou a proporção do catalisador em relação à base a média de resistência à tração foi superior com diferença estatística significativa para a média da proporção 1:1. Em relação ao fator pino, os pinos paralelo serrilhado apresentaram a maior média de resistência à tração independente da proporção base/catalisador utilizada
Ver menos
Abstract: The objective of this work was to evaluate the tensile strenght of aesthetic bolts intra-radiculares, with different forms, settled with dual resinous cement with different ratios of catalyser in relation the base. 60 bovine incisors with similar dimensions had been used. The crown was...
Ver mais
Abstract: The objective of this work was to evaluate the tensile strenght of aesthetic bolts intra-radiculares, with different forms, settled with dual resinous cement with different ratios of catalyser in relation the base. 60 bovine incisors with similar dimensions had been used. The crown was separate of the root through a diamantado record double face in the length of 16 mm from the apex. After that, all the canals radiculares had been obturados and the raÍzes had received a mark 2,0 mm simulating the amelo-cementário limit and a composed resin layer was inserted in the apical region of the root to increase the retention of the same one in the polystyrene resin block during the mechanical assay. The samples had been distributed, aleatoriamente, in six experimental groups (n=10), being that in 30 raízes the bolts had been fixed conical smooth and in the others 30 raízes the bolts parallel serrated. For the face-hardenings of the bolts, the raízes had been desobturadas in 12 mm with drill Gates Gliden n° 3 and for the preparation of the canal the specific drill for each bolt was used. Afier that, the bolts had been fixed applying the adhesive system Single Bond (3M) and the resinous cement dual Rely X (3M) with different ratios of base/catalisador (b/c): Gl - bolts parallel serrated cemented in ratio 1:1, G2 ¿bolts parallel serrated cemented in ratio 1:2, G3 - bolts parallel serrated cemented in ratio 1:3, G4 - cemented bolts conical smooth in ratio 1:1, G5 - emented bolts conical smooth in ratio 1:2, G6 - cemented bolts conical smooth in ratio 1:3. Afier storage per one week in greenhouse 37°C, the samples had been submitted to the assay of tensile strenght in a Instron the speed of 1mm/mim, until the displacement of the bolt. The data had been submitted to the variance analysis that evidenced difference significant statistics for the factors Bolts and Ratio, not having difference statistics for the interaction bolt x ratio. Better to evidence this result the test of Multiple Variation of Tukey was applied for each factor (LSMEANS) that it showed that when if tripled the ratio of the catalyser in relation to the base the average of tensile strenght was superior with difference significant statistics for the average of ratio 1:1. In relation to the factor bolt, the bolts parallel serrated had presented the average greater of independent tensile strenght of the used base/catalisador ratio
Ver menos
Worschech, Claudia Cia, 1971-
Avaliador
Efeito da proporção entre pastas base e catalisadora do cimento resinoso e da forma de pinos pre-fabricados na resistencia a tração
Monica da Consolação Canuto Salgueiro
Efeito da proporção entre pastas base e catalisadora do cimento resinoso e da forma de pinos pre-fabricados na resistencia a tração
Monica da Consolação Canuto Salgueiro
Exemplares
Nº de exemplares: 1
Não existem reservas para esta obra