Resistencia a tração do titanio comercialmente puro soldado a laser em diferentes distancias e diametros
Daniela Maffei Botega
TESE
Português
(Broch.)
T/UNICAMP B657r
[Tensile strenght of laser welded commercially pure titanium with different distances and diameters]
Piracicaba, SP : [s.n.], 2005.
75f. : il.
Orientador: Marcelo Ferraz Mesquita
Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Resumo: Este trabalho avaliou a resistência à tração e alongamento de amostras de diferentes diâmetros (1,5, 2,0 e 5,0 mm) fundidas em titânio comercialmente puro (Tritan - Dentaurum), submetidas a soldagem a laser em diferentes distâncias de soldagem (0,0 mm e 0,6 mm). Foram confeccionadas 45...
Ver mais
Resumo: Este trabalho avaliou a resistência à tração e alongamento de amostras de diferentes diâmetros (1,5, 2,0 e 5,0 mm) fundidas em titânio comercialmente puro (Tritan - Dentaurum), submetidas a soldagem a laser em diferentes distâncias de soldagem (0,0 mm e 0,6 mm). Foram confeccionadas 45 amostras, separadas em 9 grupos (n= 5): G1) diâmetro 1,5 mm controle (não submetidas à soldagem); G2) diâmetro 1,5 mm e distância zero; G3) diâmetro 1,5 mm e distância 0,6 mm; G4) diâmetro 2,0 mm (controle); G5) diâmetro 2,0 mm e distância zero; G6) diâmetro 2,0 mm e distância 0,6 mm; G7) diâmetro 5,0 mm (controle); G8) diâmetro 5,0 mm e distância zero; e G9) diâmetro 5,0 mm e distância 0,6 mm. Após a fundição, todas as amostras, exceto as dos grupos controle, foram seccionadas e unidas, utilizando-se resina acrílica autopolimerizável, para a soldagem com as seguintes especificações: 320V / 9 milisegundos (ms) (amostra de 1,5mm), 330V / 9 ms (amostra de 2,0mm) e 350V / 9 ms (amostra de 5,0mm) em um aparelho de soldagem a laser Desktop-F (Dentaurum KG). Após a soldagem, foram submetidas ao ensaio de resistência à tração até a ruptura em máquina servohidráulica (MTS 810) com velocidade de 1mm/min. As superfícies de fratura foram analisadas em microscópio eletrônico de varredura (M.E.V. ¿ JEOL). Os resultados foram submetidos à Análise de Variância e teste de Tukey (p<0,05). Os valores médios de resistência máxima à tração (MPa) revelaram que o grupo controle apresentou valores, para todos os diâmetros, estatisticamente superiores aos grupos experimentais, que não diferiram entre si, exceto para 5,0 mm de diâmetro, onde a distância de 0,6 mm apresentou maiores valores (G1- 595,64; G2- 496,46; G3- 441,04; G4- 516,54; G5- 397,85; G6- 442,15; G7- 560,19; G8- 200,88; e G9- 316,04). Os valores médios de alongamento (mm) para o grupo controle foram estatisticamente superiores aos experimentais nos diâmetros 2,0 e 5,0 mm, não havendo diferença entre os grupos no diâmetro 1,5 mm. Não houve diferença estatística entre os grupos experimentais (G1- 1,68; G2- 1,47; G3- 1,20; G4- 2,61; G5- 1,34; G6- 1,05; G7- 2,51; G8- 0,92; e G9- 1,32). As imagens revelaram eficiente penetração do laser nas amostras de 1,5 e 2,0 mm de diâmetro, e insuficiente nas de 5,0 mm de diâmetro. A resistência à tração para todos os diâmetros e o alongamento para os diâmetros 2,0 e 5,0 mm foram influenciados pela técnica de soldagem a laser de forma significativa. Dentre as amostras de 5,0 mm de diâmetro submetidas à soldagem a laser, aquelas com distância de 0,6 mm entre as partes apresentaram maior alcance do feixe de laser
Ver menos
Abstract: The aim of this study was to evaluate the tensile strength and elongation of commercially pure titanium samples (Tritan - Dentaurum), with 3 diameters (1.5, 2.0 and 5.0 mm of diameter x 42 mm length), submitted to laser welding in 2 distances of soldering (0.0 mm and 0.6 mm). 45 samples...
Ver mais
Abstract: The aim of this study was to evaluate the tensile strength and elongation of commercially pure titanium samples (Tritan - Dentaurum), with 3 diameters (1.5, 2.0 and 5.0 mm of diameter x 42 mm length), submitted to laser welding in 2 distances of soldering (0.0 mm and 0.6 mm). 45 samples were made (dumbbell), divided in 9 groups (5 each): G1) 1.5 mm control (without welding procedures); G2) 1.5 mm and no distance; G3) 1.5 mm and 0.6 mm of distance; G4) 2.0 mm (control); G5) 2.0 mm and no distance; G6) 2.0 mm and 0.6 mm; G7) 5.0 mm (control); G8) 5.0 mm and no distance; G9) 5.0 mm and 0.6 mm of distance. After casting, all the samples, except control groups, were sectioned and joined with self curing acrylic resin for the welding procedures, as follows: 320V/9 miliseconds (ms) (samples of 1.5mm), 330V/9ms (samples of 2.0 mm) and 350V/9ms (samples of 5.0 mm) using a laser welding machine Desktop-F (Dentaurum KG). After soldering, the samples were submitted to tensile test using a servohidraulic machine MTS-810 with speed of 1mm/min. The fractured surfaces were microscopically analyzed (M.E.V. ¿ JEOL). Data were submitted to ANOVA and Tukey¿s test (p<0.05). The tensile strength mean values (MPa) for control group were statistically higher than the experimental groups, which did not differ from each other, except for 5.0 mm group, in which the samples with 0.6 mm of distance had the highest values (G1- 595.64; G2- 496.46; G3- 441.04; G4- 516.54; G5- 397.85; G6- 442.15; G7- 560.19; G8- 200.88 and G9- 316.04). The mean values of elongation (mm) for the control group were statistically higher than experimental groups in the 2.0 and 5.0 mm, having no difference for the groups with 1.5 mm. There was no difference between the experimental groups (G1- 1.68; G2- 1.47; G3- 1.20; G4- 2.61; G5- 1.34; G6- 1.05; G7- 2.51; G8- 0.92; and G9- 1.32). The SEM images showed a good penetration of laser in the samples of 1.5 and 2.0 mm of diameter, and insufficient penetration of laser in the samples of 5.0 mm. Ductile fractures were predominant in all groups with the presence of dimples. Laser welding procedure is an effective method of joining titanium, however, caused a decrease in the values of tensile strength for all diameters and elongation for 2.0 and 5.0 mm. Among the 5.0 mm samples submitted to laser welding procedures, the laser welding was more effective for the samples with distance of 0.6 mm between the parts
Ver menos
Mesquita, Marcelo Ferraz, 1967-
Orientador
Vaz, Luis Geraldo
Avaliador
Ribeiro, Ricardo Faria
Avaliador
Consani, Rafael Leonardo Xediek, 1974-
Avaliador
Resistencia a tração do titanio comercialmente puro soldado a laser em diferentes distancias e diametros
Daniela Maffei Botega
Resistencia a tração do titanio comercialmente puro soldado a laser em diferentes distancias e diametros
Daniela Maffei Botega
Exemplares
Nº de exemplares: 1
Não existem reservas para esta obra