Analise longitudinal da resistencia a tração, da nanoinfiltração e do padrão morfologico da camada hibrida de sistemas adesivos autocondicionantes aplicados a dentina humana higida ou afetada por carie
Maria Carolina Guilherme Erhardt
TESE
Português
(Broch.)
T/UNICAMP Er39a
[Long-term analysis of microtensile, nanoleakage and morphologic pattern of hybrid layers promoted by different self-etching bonding agents to normal and caries-affected human dentin]
Piracicaba, SP : [s.n.], 2005.
197p. : il.
Orientadores: Luiz Andre Freire Pimenta, Roger William Fernandes Moreira
Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Resumo: O objetivo deste estudo in vitro foi determinar a durabilidade da interface adesiva emdentina normal (DN) ou afetada por cárie (DAC) promovida por um sistema adesivo simplificado convencional (AdperScotchbond1/ SB)e dois sistemas autocondicionantes de dois passos(Clearfil Protect Bond /...
Ver mais
Resumo: O objetivo deste estudo in vitro foi determinar a durabilidade da interface adesiva emdentina normal (DN) ou afetada por cárie (DAC) promovida por um sistema adesivo simplificado convencional (AdperScotchbond1/ SB)e dois sistemas autocondicionantes de dois passos(Clearfil Protect Bond / PBe AdheSE/ AD), após24 horas(24h)ou 6 meses(6me)de imersão em água.Para o teste de microtração,90 molares humanos cariados foram selecionados. A superfície dentinária foi exposta através de seccionamento com disco duplo diamantado e polimento com lixas de carbeto de silício, deixando uma área central de DAC. Osdentes foram aleatoriamente divididos em 3 grupos para que recebessem a aplicação de um dos 3 sistemas adesivos, de acordo com a recomendação dos fabricantes.Blocos de compósito Tetric Ceram com altura de 4 mm foram incrementalmente confeccionados,e após 24 h de armazenagem em água destilada a 37 oC, os dentes foram seriadamente seccionados em fatias de 1,0mm de espessura paralelas ao longo eixo dental.Em seguida,dispositivos em forma de ampulheta foram confeccionados com pontas diamantadas de granulação fina em alta rotação,com área adesiva final de aproximadamente1,0 mm2, que continham DN ou DAC. Os espécimes foram armazenados em água destilada por 24h ou 6me. Decorrido este período, os espécimes foram fixados individualmente em um dispositivo de microtração (Bencor-T),acoplado em máquina de ensaio universal (Instron), para teste à 0,5 mm/min.Após o teste, a porção dentinária dos espécimes fraturados foi avaliada em um microdurômetro do tipo Knoope também observadas em microscópio eletrônico de varredura(MEV). As médias de resistência de união foram submetidos aos testes de análise de variância (ANOVA 3 fatores),StudentNewmanKeulse t de Student(p < 0,05). Cinqüenta e quatro molares cariados adicionais foram preparados da mesma maneira supradescrita. Após 24 h de armazenagem em água destilada a 37 oC,os dentes foram seccionados em fatiasde 1,0mm de espessura paralelas ao longo eixo dental. As atias foram também armazenadas em água destilada por24h ou'6me. Os espécimes de nanoinfiltração foram imersos em solução e nitrato de prata amoniacal por 24 h, lavados abundantemente imerso sem solução foto reveladora por 8 h, sobre luz fluorescente. Após o tempo de armazenagem, fatias foram recobertas com carbono para observação em MEV. Já os espécimes de tricrômico de Masson foram manualmente polidos até que apresentassem espessura média de 3 - 5 µm, paraquefos sem corado sde acordo com as indicações da técnica histológica e visualizados em microscópio óptico. Os valores médios de microtração(MPa),foram:DN/SB/24h=42,63; DN/PB/24h= 39,18; DN/AD/24h= 28,19; DN/SB/6me= 38,43; DN/PB/6me= 39,49;DN/AD/6me=27,90;DAC/SB/24h=34,49;DAC/PB/24h=28,68;DAC/AD/24h=24,20;DAC/SB/6me=
27,76;DAC/PB/6me=24,48;DAC/AD/6me=17,24.Tantoem DNquantoem DAC,após 24h ou 6me de imersão,os sistemas SB e PB apresentaram os maiores valores de resistência de união. De uma maneira geral, maiores valores de união foram obtido sem DN, comparado à DAC.Os sistemas adesivos autocondicionantes apresentaram maior estabilidade após 6 me de armazenamento Ver menos
27,76;DAC/PB/6me=24,48;DAC/AD/6me=17,24.Tantoem DNquantoem DAC,após 24h ou 6me de imersão,os sistemas SB e PB apresentaram os maiores valores de resistência de união. De uma maneira geral, maiores valores de união foram obtido sem DN, comparado à DAC.Os sistemas adesivos autocondicionantes apresentaram maior estabilidade após 6 me de armazenamento Ver menos
Abstract: The purpose of this study was to investigate the durability of resin-dentin bonds to sound (SD) and caries-affected dentin(CAD)using an total-etch(Adper Scotchbon1d/ SB)or two self-etch bonding systems(Clearfil Protect Bond/ PBandAdheSE/ AD)bonding agents,after24 hours(24h)or 6...
Ver mais
Abstract: The purpose of this study was to investigate the durability of resin-dentin bonds to sound (SD) and caries-affected dentin(CAD)using an total-etch(Adper Scotchbon1d/ SB)or two self-etch bonding systems(Clearfil Protect Bond/ PBandAdheSE/ AD)bonding agents,after24 hours(24h)or 6 months(6mt)of storage in water.For the microtensile bond strength (Thepurposeof thisstudywasto investigatethedurabilityof resin-dentinbondstosound(SD)and caries-affected dentin(CAD)using an total-etch(AdperScotchbon1d/ SB)or two self-etch bonding systems(ClearfilProtectBond/ PBandAdheSE/ AD)bonding agents,after24hours(24h)or 6 months(6mt)of storage in water.For the microtensile bond strength(jJTBSe) valuation 90 extracted carious human molars were ground flat oclusally with wets and(SiC)papers,leaving a central region
of CAD dentin surrounded by ND.The teeth were randomly assigned into three groups,according to he bonding system used. All bonding systems were applied according to manufactures instructions. Resin composite (TetricCeram) build-ups were made incrementally. After storage in distilled water at 37°C for 24 h, teeth were erially sectioned into1.0mms labs,and trimmed to yield a 1.0mm2 bonded area that contained either NDor CAD.Experimental hlourglas specimens were stored in water
for 6 mt. Specimens that had been store din water for 24 hwere use das controls.Specimens were individually attached to a microtensile device(Bencor-T) which was coupled to an Instron machine and tested at a crosshead speed of 0.5 mm/min.The dentin surfaces of the fractured specimens were evaluated using Knoop microhardness test and observed by scanning electron microscopy( SEM).Data were analyzed by ANOVA,Student Newman Keulsandt Student multiple comparison tests (p < 0.05). Additional 54 extracted carious human molars were prepared for nanoleakage and Masson'strichrom evaluation as described above. After storage in distilled water at 37°Cfor24h, teeth were serially sectioned into1.0mm slabs that contained NDor CAD.Slabs were store dinwater for 24 h or 6 mt.The specimens for nanoleakage were immersed in ammoniacal
silver nitrate for 24 h, rinsed thoroughly and placed in photo developing solution for 8 h under fluorescent light. Slabs weres putter-coated with carbon and observed under SEM.Trichrome specimens were manually polished to 3 - 5 µm thin sections of the adhesive/denti interface and stained with the histologica dyes.Stained thin sections from each prepared tooth were imaged with optical microscopy. The µTBS mean values obtained(MPa)were:ND/SB/24h4=2.63;ND/PB/24h=
39.18; ND/AD/24h=28.19; ND/SB/6mt=38.43; ND/PB/6mt=39.49; ND/AD/6mt=27.90;
CAD/SB/24h3=4.49;CAD/PB/24h2=8.68;CAD/AD/24h2=4.20;CAD/SB/6m2t=7.76;CAD/PB/6mt= 24.48;CAD/AD/6mt= 17.24.SBandPB presented the higher µTBS values,irrespective of dentin type.Regarding bond strengths obtained with all bonding systems evaluated, it could be always observed higher mean values for ND.Self-etching bonding agents presented a higher stability after 6 mt water immersion Ver menos
of CAD dentin surrounded by ND.The teeth were randomly assigned into three groups,according to he bonding system used. All bonding systems were applied according to manufactures instructions. Resin composite (TetricCeram) build-ups were made incrementally. After storage in distilled water at 37°C for 24 h, teeth were erially sectioned into1.0mms labs,and trimmed to yield a 1.0mm2 bonded area that contained either NDor CAD.Experimental hlourglas specimens were stored in water
for 6 mt. Specimens that had been store din water for 24 hwere use das controls.Specimens were individually attached to a microtensile device(Bencor-T) which was coupled to an Instron machine and tested at a crosshead speed of 0.5 mm/min.The dentin surfaces of the fractured specimens were evaluated using Knoop microhardness test and observed by scanning electron microscopy( SEM).Data were analyzed by ANOVA,Student Newman Keulsandt Student multiple comparison tests (p < 0.05). Additional 54 extracted carious human molars were prepared for nanoleakage and Masson'strichrom evaluation as described above. After storage in distilled water at 37°Cfor24h, teeth were serially sectioned into1.0mm slabs that contained NDor CAD.Slabs were store dinwater for 24 h or 6 mt.The specimens for nanoleakage were immersed in ammoniacal
silver nitrate for 24 h, rinsed thoroughly and placed in photo developing solution for 8 h under fluorescent light. Slabs weres putter-coated with carbon and observed under SEM.Trichrome specimens were manually polished to 3 - 5 µm thin sections of the adhesive/denti interface and stained with the histologica dyes.Stained thin sections from each prepared tooth were imaged with optical microscopy. The µTBS mean values obtained(MPa)were:ND/SB/24h4=2.63;ND/PB/24h=
39.18; ND/AD/24h=28.19; ND/SB/6mt=38.43; ND/PB/6mt=39.49; ND/AD/6mt=27.90;
CAD/SB/24h3=4.49;CAD/PB/24h2=8.68;CAD/AD/24h2=4.20;CAD/SB/6m2t=7.76;CAD/PB/6mt= 24.48;CAD/AD/6mt= 17.24.SBandPB presented the higher µTBS values,irrespective of dentin type.Regarding bond strengths obtained with all bonding systems evaluated, it could be always observed higher mean values for ND.Self-etching bonding agents presented a higher stability after 6 mt water immersion Ver menos
Pimenta, Luiz Andre Freire, 1965-
Orientador
Moreira, Roger William Fernandes, 1971-
Coorientador
Sundfeld, Renato Hermann
Avaliador
Carvalho, Ricardo Marins de
Avaliador
Rontani, Regina Maria Puppin, 1959-
Avaliador
Correr Sobrinho, Lourenço, 1960-
Avaliador
Analise longitudinal da resistencia a tração, da nanoinfiltração e do padrão morfologico da camada hibrida de sistemas adesivos autocondicionantes aplicados a dentina humana higida ou afetada por carie
Maria Carolina Guilherme Erhardt
Analise longitudinal da resistencia a tração, da nanoinfiltração e do padrão morfologico da camada hibrida de sistemas adesivos autocondicionantes aplicados a dentina humana higida ou afetada por carie
Maria Carolina Guilherme Erhardt
Exemplares
Nº de exemplares: 1
Não existem reservas para esta obra