Efeito da escovação na rugosidade de superfície e desgaste do material cimentante na área de união entre o esmalte e a cerâmica vítrea CAD/CAM
Luísa de Almeida Vieira Marins
TCC
Português
TCC/UNICAMP M339e
[Effect of toothbrushing on the roughness surface and wear of cementing material at the bonded enamel - CAD/CAM glass ceramic interface]
Piracicaba, SP : [s.n.], 2022.
1 recurso on-line (31 p.) : il., digital, arquivo PDF.
Orientadores: Marcelo Giannini, Vitaliano Gomes Araújo Neto
Trabalho de Conclusão de Curso (graduação) - Universidade Estadual de Campinas (UNICAMP), Faculdade de Odontologia de Piracicaba (FOP)
Resumo: Este estudo avaliou o efeito da escovação na linha de cimentação entre esmalte e cerâmica vítrea, utilizando diferentes materiais para cimentação. Para confecção das amostras, foram utilizados 30 blocos de esmalte e 30 de cerâmica, que foram unidos com 3 tipos de agentes cimentantes: 1-...
Ver mais
Resumo: Este estudo avaliou o efeito da escovação na linha de cimentação entre esmalte e cerâmica vítrea, utilizando diferentes materiais para cimentação. Para confecção das amostras, foram utilizados 30 blocos de esmalte e 30 de cerâmica, que foram unidos com 3 tipos de agentes cimentantes: 1- cimento resinoso RelyX Ultimate (REXU), 2- cimento autoadesivo RelyX Unicem 2 (REU2) e 3- cimentação com compósito restaurador Z100 aquecido (60°C). A linha de cimentação das amostras foram escovadas e a superfície dos 3 materiais avaliadas quanto à rugosidade (RG, em µm), perfil de rugosidade (PR, em µm) e perda de volume (PV, em µm3) (antes ou "baseline", após 20 e 60 mil ciclos de escovação). Os dados foram avaliados pela Análise Linear Generalizada (dois fatores: "material" e "ciclo de escovação") e teste Bonferroni ('alfa'=0,05). REXU e Z100 exibiram menor RG que REU2, exceto após 60 mil ciclos de escovação quando apenas Z100 diferiu de REU2. A progressão da escovação aumentou a RG e PR para todos materiais. REU2 também apresentou maior PR que REXU e Z100, quando analisados em relação ao esmalte. A PV com relação ao esmalte e à cerâmica foi menor para o Z100 com 20 mil ciclos. Para 60 mil ciclos, REXU apresentou a menor PV em relação à cerâmica e o REU2 a maior PV em relação ao esmalte e cerâmica. No geral, REXU e Z100 apresentaram os melhores resultados com relação às avaliações realizadas e o REU2 os maiores valores RG, PR e PV com o aumento da escovação
Ver menos
Abstract: This study evaluated the effect of toothbrushing on enamel-cementing material-ceramic bonded interfaces, using different cementing materials. Thirty enamel and thirty ceramic blocks were bonded with three types of cementing materials to produce the samples that were bonded with 3 cementing...
Ver mais
Abstract: This study evaluated the effect of toothbrushing on enamel-cementing material-ceramic bonded interfaces, using different cementing materials. Thirty enamel and thirty ceramic blocks were bonded with three types of cementing materials to produce the samples that were bonded with 3 cementing materials: 1- resin cement RelyX Ultimate (REXU), 2- self-adhesive resin cement RelyX Unicem 2 (REU2) and 3- heated Z100 restorative composite (60°C). Bonded interfaces of the samples were toothbrushed and the surfaces of the 3 cementing materials were evaluated for roughness (RG, in µm), roughness profile (RP, in µm) and volume loss (VL, in µm3) (before or baseline and after 20,000 and 60,000 toothbrushing cycles). Data were evaluated by Generalized Linear Analysis (two factors: "material" and "toothbrushing cycle") and Bonferroni test ('alpha'=0.05). REXU and Z100 exhibited lower RUS than that presented by REU2, except after 60,000 toothbrushing cycles when only Z100 differed from REU2. The increase in toothbrushing cycles increased the RG and RP for all materials. REU2 also showed higher RP than those sowed by REXU and Z100, when analyzed regarding the enamel. The VL of Z100 was the lowest with 20,000 toothbrushing cycles, regarding the enamel and ceramic. For 60,000 cycles, REXU showed the lowest VL regarding the ceramic and REU2 the highest VLO regarding the enamel and ceramic. In general, REXU and Z100 showed the best results regarding the evaluations performed and the REU2 exhibited the greatest RG, RP and VL
Ver menos
Agência de fomento: CNPq
Número do processo: 134233/2020-4
Requisitos do sistema: Software para leitura de arquivo em PDF
Aberto
Giannini, Marcelo, 1969-
Orientador
Araújo Neto, Vitaliano Gomes de, 1994-
Coorientador
Ferretti, Marcela Alvarez, 1991-
Avaliador
Santi, Marina Rodrigues, 1994-
Avaliador
Efeito da escovação na rugosidade de superfície e desgaste do material cimentante na área de união entre o esmalte e a cerâmica vítrea CAD/CAM
Luísa de Almeida Vieira Marins
Efeito da escovação na rugosidade de superfície e desgaste do material cimentante na área de união entre o esmalte e a cerâmica vítrea CAD/CAM
Luísa de Almeida Vieira Marins