Resistencia inicial a remoção, por tração axial, de parafusos de titanio, de 2mm de diametro, inseridos bicorticalmente em tibias de coelhos
Claudia Jordão Silva
TESE
Português
(Enc.)
T/UNICAMP Si38r
Piracicaba, SP : [s.n.], 1998.
123f. : il.
Orientador: Luis Augusto Passeri
Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Resumo: O propósito do presente trabalho foi avaliar a resistência inicial à remoção por tração axial, de parafusos de Titânio de 2mm de diâmetro, inseridos de modo bicortical, em tíbias congeladas de coelhos da raça Nova Zelândia. Foram testados 30 parafusos de 3 marcas comerciais diferentes,...
Ver mais
Resumo: O propósito do presente trabalho foi avaliar a resistência inicial à remoção por tração axial, de parafusos de Titânio de 2mm de diâmetro, inseridos de modo bicortical, em tíbias congeladas de coelhos da raça Nova Zelândia. Foram testados 30 parafusos de 3 marcas comerciais diferentes, confeccionados em titânio comercialmente puro e divididos em 3 grupos (I - Engimplan, II - Synthes e III - Bucomax). Para todos os grupos as tíbias foram perfuradas em ambas as corticais, e após a utilização dos respectivos obtentores de rosca, os parafusos foram inseridos e rosqueados através de chave manual. A seguir, cada tíbia foi seccionada com disco de carborundum em ambas as extremidades e posicionada sobre uma placa de cera utilidade. Após a inclusão em resina acrílica ativada quimicamente, os corpos-de-prova foram submetidos, imediatamente, ao teste de resistência inicial à remoção por tração axial, a uma velocidade de 6 mm/minuto. Os resultados obtidos em quilograma-força (kgf) foram analisados através da Prova de Kruskal- Wallis, em uma prova bilateral, ao nível de 5% de probabilidade. Os resultados indicaram diferenças significantes entre a tração exercida para a remoção das diferentes marcas de parafusos, sendo que, a mais elevada foi relacionada aos parafusos da marca comercial Synthes e a mais baixa, aos parafusos da marca comercial Bucomax
Ver menos
Abstract: The purpose of the present work was to evaluate the initial resistance to the removal through traction, of 2 mm diameter Titanium screws, inserted bicortically into the frozen tibias of 30 New Zealand Breed of rabbits. Thirty screws, 10 in each of 3 different commercial marks, were tested....
Ver mais
Abstract: The purpose of the present work was to evaluate the initial resistance to the removal through traction, of 2 mm diameter Titanium screws, inserted bicortically into the frozen tibias of 30 New Zealand Breed of rabbits. Thirty screws, 10 in each of 3 different commercial marks, were tested. All of them were made of pure Titanium. In all of the groups (I, II and III) the tibias were perforated in both cortical plates and after the use of the respective thread taps, the screws were inserted and tightened with a screwdriver. Then each tibia was cut with a carborundum disk at both ends and positioned on a wax plate stick and a PVC cylinder was placed over the tibia and screw. After this there was inclusion of chemically activated acrylic resin to the samples, the test bodies were immediately submitted to the removal traction resistance test by the universal rehearsal machine, at the speed of 6 mm /minute. The results obtained in kilogram-force (kgf) and were analyzed through a bilateral test, the Kruskal-Wallis's Test, at a 5% level of probability. The results indicated significant differences among the tensile exerted needed for the removal of the screws. The largest force was related to the group II screws (Synthes) while the smallest to the Group III screws (Bucomax)
Ver menos
Resistencia inicial a remoção, por tração axial, de parafusos de titanio, de 2mm de diametro, inseridos bicorticalmente em tibias de coelhos
Claudia Jordão Silva
Resistencia inicial a remoção, por tração axial, de parafusos de titanio, de 2mm de diametro, inseridos bicorticalmente em tibias de coelhos
Claudia Jordão Silva
Exemplares
Nº de exemplares: 1
Não existem reservas para esta obra