Decomposição catalitica de hidrazina sobre carbetos e nitretos de tungstenio
João Batista Oliveira dos Santos
DISSERTAÇÃO
Português
(Broch.)
T/UNICAMP Sa59d
Campinas, SP : [s.n.], 1998.
79f. : il.
Orientadores: Gustavo Paim Valença, Jose Augusto Jorge Rodrigues
Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica
Resumo: WC e 'beta¿-'W IND. 2¿¿N¿ em pó, passivados e não passivados, foram preparados através de reação a temperatura programada. Para a síntese do carbeto utilizou-se o 'W¿¿O IND. 3¿ e uma mistura de 'C¿¿H IND. 4¿/¿H IND.2¿, já a obtenção do nitreto envolveu a reação entre o 'W¿¿O IND. 3¿ e 'N¿¿H...
Ver mais
Resumo: WC e 'beta¿-'W IND. 2¿¿N¿ em pó, passivados e não passivados, foram preparados através de reação a temperatura programada. Para a síntese do carbeto utilizou-se o 'W¿¿O IND. 3¿ e uma mistura de 'C¿¿H IND. 4¿/¿H IND.2¿, já a obtenção do nitreto envolveu a reação entre o 'W¿¿O IND. 3¿ e 'N¿¿H IND. 3¿. Através da adsorção de N2 constatou-se que a área específica do nitreto (~50 'm POT. 2¿¿g POT. ¿ 1¿) diminui 20% após a etapa de passivação, enquanto que a do carbeto (~15 'm POT. 2¿¿g POT. ¿ 1¿) parece não sofrer influência do oxigênio adsorvido na passivação. Por outro lado, verificou-se que o carbono em excesso na superfície do carbeto diminui a área específica em 40%. Este carbono foi removido através de uma redução com 'H IND. 2¿ a 998 K durante 95 minutos e constatou-se, através de difração de raios-X, que este tratamento não interfere na estrutura, hexagonal compacta, original do carbeto ... Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital
Ver menos
Abstract: WC and 'beta¿-'W IND. 2¿N were prepared by temperature prograrnrned reaction. After the reaction, some samples of WC or 'beta¿-'W IND. 2¿¿N¿ were passivated at room temperature with a mixture of 1% p/p 'O IND. 2¿ in He. The carbide was prepared from 'W¿¿O IND. 3¿ and a mixture of 'C¿¿H...
Ver mais
Abstract: WC and 'beta¿-'W IND. 2¿N were prepared by temperature prograrnrned reaction. After the reaction, some samples of WC or 'beta¿-'W IND. 2¿¿N¿ were passivated at room temperature with a mixture of 1% p/p 'O IND. 2¿ in He. The carbide was prepared from 'W¿¿O IND. 3¿ and a mixture of 'C¿¿H IND. 4¿/¿H IND. 2¿. The nitride was prepared by the reaction of 'W¿O IND. 3¿ and pure 'N¿¿H IND. 3¿. The nitride specific BET surface area, measured by 'N IND. 2¿ adsorption, was ~50 'm POT. 2¿¿g IND. ¿1¿ and decreased ca. 20% after passivation, while the carbide BET surface area (~15 'm IND. 2¿¿g IND. ¿1¿) did not diminish by the adsorbed oxygen during the passivation step. On the other hand, excess carbon on the surface of the carbide reduces de BET specific surface area in 40%. Removal of the excess carbon in flowing 'H IND. 2¿ at 998 K for 95 rninutes did not change the hexagonal structure of the carbide, as observed using X-ray diffraction
Ver menos
Valença, Gustavo Paim, 1960-
Orientador
Rodrigues, José Augusto Rosário, 1941-2019
Coorientador
Cruz, Gilberto Marques da
Avaliador
Gomez Cobo, Antonio José, 1957-
Avaliador
Decomposição catalitica de hidrazina sobre carbetos e nitretos de tungstenio
João Batista Oliveira dos Santos
Decomposição catalitica de hidrazina sobre carbetos e nitretos de tungstenio
João Batista Oliveira dos Santos
Exemplares
Nº de exemplares: 2
Não existem reservas para esta obra