Physical properties of antiferromagnetic single crystal GdIn3
L. S. Silva, E. B. Peixoto, S. G. Mercena, A. A. Coelho, C. T. Meneses, J. G. S. Duque
ARTIGO
Inglês
Abstract: A sample of GdIn3 was obtained via the metallic flux technique and its structural, magnetic, and thermodynamic properties were studied. X-ray diffraction (XRD) measurements realized at room temperature were performed in order to verify whether the desired crystalline phase had been...
Ver mais
Abstract: A sample of GdIn3 was obtained via the metallic flux technique and its structural, magnetic, and thermodynamic properties were studied. X-ray diffraction (XRD) measurements realized at room temperature were performed in order to verify whether the desired crystalline phase had been obtained. The experimental results show that single crystals were grown successfully by the employed growth technique. The magnetic characterization was carried out through magnetic susceptibility data as a function of temperature (2 <= x <= 300 K) and magnetic field (-7 <= H <= 7 T). The specific heat was measured using a commercial small mass calorimeter that employed the thermal relaxation technique in the temperature range of 2-200 K
Ver menos
Fechado
Physical properties of antiferromagnetic single crystal GdIn3
L. S. Silva, E. B. Peixoto, S. G. Mercena, A. A. Coelho, C. T. Meneses, J. G. S. Duque
Physical properties of antiferromagnetic single crystal GdIn3
L. S. Silva, E. B. Peixoto, S. G. Mercena, A. A. Coelho, C. T. Meneses, J. G. S. Duque
Fontes
Materials letters (Fonte avulsa) |