To evaluate whether biaxial flexural strength (BFS) of dual resin cements is affected by light absence or attenuation, storage time, or cements' chemical nature. One hundred and twenty disk-shaped specimens were made from each cement (non-self-adhesive cement and self-adhesive cement) using Teflon...

To evaluate whether biaxial flexural strength (BFS) of dual resin cements is affected by light absence or attenuation, storage time, or cements' chemical nature. One hundred and twenty disk-shaped specimens were made from each cement (non-self-adhesive cement and self-adhesive cement) using Teflon molds on a controlled temperature surface (35 degrees C). Specimens were polymerized as follows (N = 30): self-cured, directly light-cured, light-cured at a distance of 6 mm between the light tip and the specimen, and through a 6-mm thick composite resin barrier (indirectly light-cured). Each group was divided (N = 10) for storage purposes (15 minutes, 24 hours, and 6 months). Specimens were placed into a biaxial-flexure jig and a vertical load was applied until failure. The BFS values were subjected to generalized linear models statistical analysis and Weibull distributions (alpha = 0.05). After 15 minutes aging, neither material achieved enough polymerization to perform the BFS test when polymerized using the self-curing mode. The self-adhesive product demonstrated much lower variation in strength with storage time than did the non-self-curing cement. Attenuated/light-curing reduced BFS values only for 15-minutes storage period for both materials. Flexural strength of the self-adhesive cement was less affected by light absence/attenuation and storage time

COORDENAÇÃO DE APERFEIÇOAMENTO DE PESSOAL DE NÍVEL SUPERIOR - CAPES

Fechado