This study aimed to objectively evaluate the radiopacity of different dental composites and their subjective influence on diagnosing secondary caries-like lesions and how these results correlate. For objective analysis, three resin specimens (1 mm thick, with a 4-mm internal diameter) were made with...

This study aimed to objectively evaluate the radiopacity of different dental composites and their subjective influence on diagnosing secondary caries-like lesions and how these results correlate. For objective analysis, three resin specimens (1 mm thick, with a 4-mm internal diameter) were made with four composites: 1) Charisma; 2) Filtek Z250; 3) Prisma AP.H; and 4) Glacier. Three human teeth were selected and then mesio-distally sectioned (1 mm thick) to make the dental specimens. An aluminum (Al) wedge (12 steps, 1 mm thick, 99.8% purity) was used as an internal standard to calculate the radiopacity. were selected and then prepared with a mesio-occluso-distal (MOD) inlay cavity, with half the teeth receiving a round cavity to simulate the carious lesion. The MOD was restored using the cornposites at four different times. Standardized radiographs were acquired and then digitized (300 dpi and eight-bit TIFF) for both analyses. A histogram objectively measured the pixel intensity values of the images, which were converted into millimeters of Al using linear regressions. Eight observers subjectively evaluated the images using a five-point rating scale to diagnose the caries. The data were statistically analyzed using the Student t-test, the Kappa test, diagnostic testing, and the Pearson correlation coefficient (alpha=0.05). All materials showed radiopacity values compatible with dental tissues (p>0.05); Glacier was similar to dentin and Prisma AP.H was similar to enamel, while the remaining materials showed a middle radiopacity. Prisma AP.H and Glacier differed (p<0.05) in relation to their accuracy to caries diagnosis, with Glacier having greater accuracy. There was a correlation between objective and subjective analyses with negative linear dependence. An increase in the material's radiopacity could have a subjectively negative influence on the diagnosis of secondary caries; thus, an ideal radiopacity for a dental composite is closer to the dentin image and produces similar attenuation to X-rays than does dentin

Fechado