This study aimed to evaluate the effect of poly(dimethylsiloxane) on the mechanical properties of chitosan-alginate (CA) polyelectrolyte complexes (PECs) with potential application as wound dressing biomaterials. For that purpose, different amounts of poly(dimethylsiloxane) were incorporated during...

This study aimed to evaluate the effect of poly(dimethylsiloxane) on the mechanical properties of chitosan-alginate (CA) polyelectrolyte complexes (PECs) with potential application as wound dressing biomaterials. For that purpose, different amounts of poly(dimethylsiloxane) were incorporated during the formulation of the PECs. Results showed that the highest tensile strength was observed when using 0.1 g of poly(dimethylsiloxane) per gram of PEC (CAS10). This formulation was also non-hemolytic, capable of inducing thrombus formation to potentially reduce bleeding, and additionally presented high stability when exposed to physiological fluids and/or conditions simulating patient bathing. To improve its wound healing capacity, this formulation was loaded with thymol and beta-carotene (anesthetic, anti-inflammatory and antioxidant compounds) by the supercritical carbon dioxide impregnation/deposition (SSI/D) method at 250 bar and 45 °C for 14 h and at two depressurization rates (5 and 10 bar/min). The PECs were also loaded by conventional impregnation in solution for comparison purposes. Higher bioactive loadings, of 1.8 ± 0.2 and 1.3 ± 0.03 μg per milligram of PEC for thymol and beta-carotene, respectively, were observed when using SSI/D and a higher depressurization rate (10 bar/min). These values do not correspond to the maximum loaded amount of each bioactive, which were strongly retained in the PEC structure due to favorable bioactive-polymer interactions, originating matrices that should present a more sustained release during in vivo applications

CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO - CNPQ

152053/2014-0; 118607/2014-6; 308871/2012-0; 483787/2013-2; 307139/2015-8

COORDENAÇÃO DE APERFEIÇOAMENTO DE PESSOAL DE NÍVEL SUPERIOR - CAPES

7134/13-4

FUNDAÇÃO DE AMPARO À PESQUISA DO ESTADO DE SÃO PAULO - FAPESP

2015/25133-9

Fechado