PHEMA hydrogels
ARTIGO
Inglês
Hydrogels of poly (2-hydroxyethyl methacrylate) (pHEMA) are suitable materials for medical applications. Synthesis, structural characterization, kinetic, physical properties and cell viability of these materials are reported in this article. The system was conducted via free radical polymerization...
Hydrogels of poly (2-hydroxyethyl methacrylate) (pHEMA) are suitable materials for medical applications. Synthesis, structural characterization, kinetic, physical properties and cell viability of these materials are reported in this article. The system was conducted via free radical polymerization in the absence of solvents or cross-linking agents. Hydrogels were obtained with excellent dimensional stability and high thermal stability (738 K), glass transition temperature of approximately 375 K and a degree of swelling of 66 ± 4 % in ethanol. The conversion of C=C double bond of the monomer 2-hydroxyethyl methacrylate was confirmed by Fourier transform infrared spectroscopy. Results showed dense and rough morphologies in the pHEMA, presence of high molecular interactions and good resistance to various organic solvents. In vitro tests showed excellent cell viability. The materials did not display cytotoxicity, and cells proliferated and adhered at a satisfactory rate on the hydrogel. These materials have great potential for biomedical application
CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO - CNPQ
573661/2008-1
FUNDAÇÃO DE AMPARO À PESQUISA DO ESTADO DE SÃO PAULO - FAPESP
2008/57860-3; 2011/18525-7
Fechado
PHEMA hydrogels
PHEMA hydrogels
Fontes
Journal of thermal analysis and calorimetry Vol. 125 (July, 2016), p. 361-368 |