Surface modification of Ti-30Ta alloy by electrospun PCL deposition
ARTIGO
Inglês
In this study, PCL electrospun fibers were deposited on the Ti-30Ta alloy for change the surface properties. Experimental Ti-30Ta alloy was obtained by melting titanium and tantalum in arc melting furnace with argon atmosphere. Ingots were homogenized and bars with 10 mm of diameter were obtained in...
In this study, PCL electrospun fibers were deposited on the Ti-30Ta alloy for change the surface properties. Experimental Ti-30Ta alloy was obtained by melting titanium and tantalum in arc melting furnace with argon atmosphere. Ingots were homogenized and bars with 10 mm of diameter were obtained in rotative swagging. PCL fibers were deposited on disks of the alloy by electrospinning. Plasma treatment was carried out for change PCL electrospun superficial energy by using stainless steel plasma reactor. Samples were immersed in mineralization solution for apatite growth. Surfaces were evaluated by using SEM, X-rays diffraction and contact angle. Samples exhibited hydrophilic behavior after plasma treatment and mineralization. Results are very interesting for biomedical applications
CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO - CNPQ
FUNDAÇÃO DE AMPARO À PESQUISA DO ESTADO DE SÃO PAULO - FAPESP
Fechado
Surface modification of Ti-30Ta alloy by electrospun PCL deposition
Surface modification of Ti-30Ta alloy by electrospun PCL deposition
Fontes
Materials science forum Vol. 869 (Aug., 2016), p. 930-934 |