Mechanical properties of thixoformed hypoeutectic gray cast iron
Nadal R.L., Roca A.S., Fals H.D.C., Zoqui E.J.
ARTIGO
Inglês
Agradecimentos: The authors would like to thank José Maria Marquiori of Venturoso, Valentini & Cia Ltd., for producing the raw material used in this study. We are also indebted to CAPES (The Federal Agency for the Support and Assessment of Postgraduate Education, Brazil – Project CAPES/MES-Cuba no....
Ver mais
Agradecimentos: The authors would like to thank José Maria Marquiori of Venturoso, Valentini & Cia Ltd., for producing the raw material used in this study. We are also indebted to CAPES (The Federal Agency for the Support and Assessment of Postgraduate Education, Brazil – Project CAPES/MES-Cuba no. 095/2010) and CNPq (The National Council for Scientific and Technological Development, Brazil, Project PQ no. 306896/2013-3) for providing technical and financial support
Ver menos
The effects of thixoforming process variables on the final mechanical properties of a specially designed hypoeutectic cast iron were studied. An Fe-2.6 wt%C-1.5 wt%Si alloy was prepared using conventional sand casting molds and thixoformed in an eccentric press. Different temperatures and...
Ver mais
The effects of thixoforming process variables on the final mechanical properties of a specially designed hypoeutectic cast iron were studied. An Fe-2.6 wt%C-1.5 wt%Si alloy was prepared using conventional sand casting molds and thixoformed in an eccentric press. Different temperatures and heat-treatment holding times were tested. After being heated to the semisolid state at 1160 °C and 1180 °C and held at these temperatures for 0, 30, 60 and 90 s, the samples were subjected to the thixoforming process. The holding time in the semisolid range simulates the industrial heating process, which is time controlled rather than temperature controlled. The results indicate that the forces applied during thixoforming are closely related to the liquid fraction of the hypoeutectic gray cast iron. A comparative analysis of the behavior of the tensile properties, Vickers microhardness and porosity before and after thixoforming was carried out. The stress-strain curves were similar for the different liquid fractions studied: at 1160 °C the average values were YE = 282 MPa, UTS = 289 MPa, E = 0.21% and Vickers microhardness = 274HV, while at 1180 °C the corresponding figures were YE = 272 MPa, UTS = 277 MPa, E = 0.2% and Vickers microhardness = 257HV. The small variations in tensile properties can be attributed to the final graphite morphology of the thixoformed alloy. The results also show that after thixoforming, the porosity of the Fe-2.6 wt%C-1.5 wt%Si alloy decreased for all experimental conditions and had a maximum value of 5%. There was no significant difference in hardness between the thixoformed material and the as-cast alloy
Ver menos
CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO - CNPQ
306896/2013-3
COORDENAÇÃO DE APERFEIÇOAMENTO DE PESSOAL DE NÍVEL SUPERIOR - CAPES
Fechado
Mechanical properties of thixoformed hypoeutectic gray cast iron
Nadal R.L., Roca A.S., Fals H.D.C., Zoqui E.J.
Mechanical properties of thixoformed hypoeutectic gray cast iron
Nadal R.L., Roca A.S., Fals H.D.C., Zoqui E.J.
Fontes
Journal of materials processing technology Vol. 226 (Dec., 2015), p. 146-156 |