Growth direction and Si alloying affecting directionally solidified structures of Al–Cu–Si alloys
ARTIGO
Inglês
Agradecimentos: The authors acknowledge the financial support provided by IFPA (Federal Institute of Education, Science and Technology of Pará), UFPA (Federal University of Pará), FAPESP – São Paulo Research Foundation, Brazil (grants nos. 2013/09267-0 and 2013/23396-7) and CNPq (The Brazilian...
Agradecimentos: The authors acknowledge the financial support provided by IFPA (Federal Institute of Education, Science and Technology of Pará), UFPA (Federal University of Pará), FAPESP – São Paulo Research Foundation, Brazil (grants nos. 2013/09267-0 and 2013/23396-7) and CNPq (The Brazilian Research Council)
The roles of growth direction and Si content on the columnar/equiaxed transition and on dendritic spacings of Al–Cu–Si alloys still remain as an open field to be studied. In the present investigation, Al–6 wt-%Cu–4 wt-%Si and Al–6 wt-%Cu alloys were directionally solidified upwards and horizontally...
The roles of growth direction and Si content on the columnar/equiaxed transition and on dendritic spacings of Al–Cu–Si alloys still remain as an open field to be studied. In the present investigation, Al–6 wt-%Cu–4 wt-%Si and Al–6 wt-%Cu alloys were directionally solidified upwards and horizontally under transient heat flow conditions. The experimental results include tip growth rate and cooling rates, optical microscopy, scanning electron microscopy energy dispersive spectrometry and dendrite arm spacings. It was found that silicon alloying contributes to significant refinement of primary/secondary dendritic spacings for the upward configuration as compared with corresponding results of the horizontal growth. Experimental growth laws are proposed, and the effects of the presence/absence of solutal convection in both growth directions are discussed
FUNDAÇÃO DE AMPARO À PESQUISA DO ESTADO DE SÃO PAULO - FAPESP
2013/09267-0; 2013/23396-7
CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO - CNPQ
Fechado
Growth direction and Si alloying affecting directionally solidified structures of Al–Cu–Si alloys
Growth direction and Si alloying affecting directionally solidified structures of Al–Cu–Si alloys
Fontes
Materials science and technology Vol. 31, no. 9 (July, 2015), p. 1103-1112 |