Estudo "in vitro" da rugosidade produzida pela escovação na superficie de resinas compostas
Rosana Ono
TESE
Português
T/UNICAMP On6e
Piracicaba, SP : [s.n.], 1997.
153f. : il.
Orientador: Simonides Consani
Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Resumo: Este trabalho avaliou a rugosidade superficial dos compósitos Herculite XR V, Z 100 e T etric, acabados e polidos, sob a ação dentifiicio escova dental. Foram confeccionadas 56 amostras de cada material (8 mm de diâmetro por 2 mm de espessura) com preenchimento incremental da matriz e...
Ver mais
Resumo: Este trabalho avaliou a rugosidade superficial dos compósitos Herculite XR V, Z 100 e T etric, acabados e polidos, sob a ação dentifiicio escova dental. Foram confeccionadas 56 amostras de cada material (8 mm de diâmetro por 2 mm de espessura) com preenchimento incremental da matriz e exposição individual de 60 segundos, com fotopolimerizador Visilux 2 (3M). As amostras foram removidas da matriz e armazenadas em estufa a 37° C e umidade relativa de 100%, por 24 horas. Para cada tipo de compósito, 8 amostras não receberam acabamento e polimento e as 48 amostras restantes foram divididas em grupos e submetidas aos procedimentos de acabamento e polimento realizados por 2 minutos, respectivamente com aparelho de alta velócidade de rotação (Turbina DABI ATLANTE), refrigerados com água/ar, com movimentos lineares em uma única direção, e contra-ângulo (Micromotor - DABI ATLANTE) em baixa velocidade de rotação à seco. Quatro amostras de cada material sem acabamento e polimento foram submetidos à ação abrasiva da escova dental (controle), utilizando água destilada. As outras 4 amostras restantes foram submetidas ao ensaio de abrasão com solução aquosa de dentifiicio. As 48
amostras com acabamento e polimento taÍnbém submetidas ao ensaio de abrasão, çnde 24 amostras foram escovadas com água (controle) e 24 foram submetidas à escovação, com solução aquosa de entifrício. Foi utilizada máquina de escovação Equilabor, com capacidade para 8 amostras. Foram utilizadas escovas dentais Oral-B 30, associadas ao dentifrício Kolynos Super Branco. As amostras foram submetidas à movimentos lineares de escovação, com velocidade de 250 movimentos por minuto, durante 2 horas, totalizando 30.000 ciclos por amostra, desenvolvido sob a ação de uma carga axial de 200 g. As superficies das amostras foram avaliadas antes e após cada procedimento e a leitura considerada foi a média aritmética entre os picos e vales (Ra), percorrida pelo perfilômetro (Prazis-Rug-3 Argentina), num trecho de 4,8 mm. A rugosidade da superficie resultante do uso da tira de poliéster, tira + água e tira + dentifrício não mostrou diferença estatisticamente significativa para a resina Z 100. A maior média de rugosidade superficial foi obtida na técnica pontas diamantadas F, FF + abrasivos de silicone Viking (cinza e verde) e gel + dentifrício, em todos os compósitos estudados. Observou-se também que, a restauração sem
polimento mecânico suporta melhor a ação da escovação com dentifrício, e na restauração polida mecanicamente, a escovação com dentifrício produziu resultados mais críticos Ver menos
amostras com acabamento e polimento taÍnbém submetidas ao ensaio de abrasão, çnde 24 amostras foram escovadas com água (controle) e 24 foram submetidas à escovação, com solução aquosa de entifrício. Foi utilizada máquina de escovação Equilabor, com capacidade para 8 amostras. Foram utilizadas escovas dentais Oral-B 30, associadas ao dentifrício Kolynos Super Branco. As amostras foram submetidas à movimentos lineares de escovação, com velocidade de 250 movimentos por minuto, durante 2 horas, totalizando 30.000 ciclos por amostra, desenvolvido sob a ação de uma carga axial de 200 g. As superficies das amostras foram avaliadas antes e após cada procedimento e a leitura considerada foi a média aritmética entre os picos e vales (Ra), percorrida pelo perfilômetro (Prazis-Rug-3 Argentina), num trecho de 4,8 mm. A rugosidade da superficie resultante do uso da tira de poliéster, tira + água e tira + dentifrício não mostrou diferença estatisticamente significativa para a resina Z 100. A maior média de rugosidade superficial foi obtida na técnica pontas diamantadas F, FF + abrasivos de silicone Viking (cinza e verde) e gel + dentifrício, em todos os compósitos estudados. Observou-se também que, a restauração sem
polimento mecânico suporta melhor a ação da escovação com dentifrício, e na restauração polida mecanicamente, a escovação com dentifrício produziu resultados mais críticos Ver menos
Abstract: The purpose of the present study was to evaluate the surface roughness of Herculite XR V, Z 100 and T etric composite samples, finished and polished under the action of the tooth-brushltoothpaste binomial. A set of fifty-six 8 mm diameter, 2 mm thick samples was prepared for each studied...
Ver mais
Abstract: The purpose of the present study was to evaluate the surface roughness of Herculite XR V, Z 100 and T etric composite samples, finished and polished under the action of the tooth-brushltoothpaste binomial. A set of fifty-six 8 mm diameter, 2 mm thick samples was prepared for each studied material, using the incremental technique for mold filling. A sixty second exposure to visible light was used to set the samples. The activating . unit used was Visilux 2 (3M): After setting, the samples were stored in an oven, at 37° C and 100% relative humidity for 24 hours. Eight samples of each material were not subjected to the finishing and polishing procedures. The left ones, 48 samples, were divided into groups and subjected to the procedures above mentioned with differeÍlt kinds of abrasives. Each fmishing and polishing procedure lasted approximately 2 minutes. The finishing procedure was carried out with the aid of an air-water spray, high speed handpiece, moved straight on a one and on1y direction. An air-cooled,
low-speed handpiece was used for the polishing procedures. Four samples of each material not subjected to the finishing and polishing procedures (control groups) were brushed on1y with distilled water. The other four non finished samples were brushed with an aque'ous solution of a toothpaste. The 48 samples subjected to the finishing and polishing procedures were also, brushed with water (24 samples) or an aqueous solution of a toothpaste (the other 24 samples). A national brushing machine (Equilabor) holding 8 samples was used. Oral 30 tooth-brushes were used with Kolynos Super Branco toothpaste. The samples were brushed in a straight and only direction. The electric motor produced 250 strokes/minute and the machine was activated until the counter registered 30,000 strokes. The load of the I brush was 200 g, and 4.6 ml (6 g) of the toothpaste diluted in 6 ml of ; distilled water was used. The surfaces of the samples were evaluated before I and after each procedure and. the reading that was used was the rithmetic I mean value between the peaks and valleys scanned by the surface texture measuring instrument (Prazis-Rug3-Argentina) on a 4,8 mm path length. The results, the roughness produced by the polyester strip, polyester strip plus water and polyester strip plus toothpaste' did not show any significant statistical difference to Z 100 resin. The roughest surface was obtained when F and FF diamond
points plus Viking abrasives (grey and green) and gel plus toothpaste were applied to alI the studied composites. It was also observed that the restoration not polished bears the tooth-brush action better and that the use of a tooth-brush produced worse results in the polished restorations Ver menos
low-speed handpiece was used for the polishing procedures. Four samples of each material not subjected to the finishing and polishing procedures (control groups) were brushed on1y with distilled water. The other four non finished samples were brushed with an aque'ous solution of a toothpaste. The 48 samples subjected to the finishing and polishing procedures were also, brushed with water (24 samples) or an aqueous solution of a toothpaste (the other 24 samples). A national brushing machine (Equilabor) holding 8 samples was used. Oral 30 tooth-brushes were used with Kolynos Super Branco toothpaste. The samples were brushed in a straight and only direction. The electric motor produced 250 strokes/minute and the machine was activated until the counter registered 30,000 strokes. The load of the I brush was 200 g, and 4.6 ml (6 g) of the toothpaste diluted in 6 ml of ; distilled water was used. The surfaces of the samples were evaluated before I and after each procedure and. the reading that was used was the rithmetic I mean value between the peaks and valleys scanned by the surface texture measuring instrument (Prazis-Rug3-Argentina) on a 4,8 mm path length. The results, the roughness produced by the polyester strip, polyester strip plus water and polyester strip plus toothpaste' did not show any significant statistical difference to Z 100 resin. The roughest surface was obtained when F and FF diamond
points plus Viking abrasives (grey and green) and gel plus toothpaste were applied to alI the studied composites. It was also observed that the restoration not polished bears the tooth-brush action better and that the use of a tooth-brush produced worse results in the polished restorations Ver menos
Consani, Simonides, 1939-
Orientador
Goes, Mario Fernando de, 1954-
Avaliador
Nóbilo, Mauro Antonio de Arruda, 1965-
Avaliador
Pedrosa, Sergio de Freitas
Avaliador
Estudo "in vitro" da rugosidade produzida pela escovação na superficie de resinas compostas
Rosana Ono
Estudo "in vitro" da rugosidade produzida pela escovação na superficie de resinas compostas
Rosana Ono