Type: Artigo de periódico
Author: Kantovitz, KR
Pascon, FM
Correr, GM
Alonso, RCB
Rodrigues, LKA
Alves, MC
Puppin-Rontani, RM
Abstract: Objectives: The aim of this study was to determine the effect of environmental conditions on the degradation of ionomeric and resin sealant materials. Material and Methods: FluroShield, Vitremer, and Ketac Molar disc-shaped specimens (n=18/material) were prepared, polished, subjected to initial hardness and roughness readings. Six discs of each material were randomly assigned to one of three different storage solutions: 0.3% citric acid (CA), demineralization solution (DE), and remineralization solution (RE). The specimens were individually immersed in 3 mL of the test solutions, which were daily changed. After 15 days of storage, new surface roughness and hardness readings were done. Fluoride release in the solutions was measured within 15 days. Data were analyzed by ANOVA and Tukey's and Contrast tests (alpha=0.05). Results: The storage in CA increased the roughness of Vitremer and Ketac Molar. A significant reduction in hardness was observed for all materials after storage in all solutions. For all materials, the greatest amounts of fluoride release occurred during the 1(st) day. FluroShield presented the same patterns of fluoride release in all solutions. Ketac Molar and Vitremer released the highest amounts of fluoride in the CA solution. Conclusions: Ionomeric materials are more susceptible to degradation than resin-based materials under acidic conditions. Acidic conditions lead to a higher fluoride release from ionomeric materials.
Subject: Environmental biodegradation
Fissure sealant
Country: Brasil
Editor: Univ Sao Paulo Fac Odontologia Bauru
Citation: Journal Of Applied Oral Science. Univ Sao Paulo Fac Odontologia Bauru, v. 17, n. 4, n. 294, n. 300, 2009.
Rights: fechado
Date Issue: 2009
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000269124200006.pdf153.93 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.