Title: Evolution of Eutectic Spacing During Unidirectional Solidification of Al-Ni Alloys
Author: Araujo, IJC
da Silva, BL
Spinelli, JE
Garcia, A
Abstract: Hypoeutectic Al-Ni alloys show a ductile phase alpha distributed with a beta phase Al3Ni fragile where beta serves as reinforcement of the structure of the material. The eutectic composition alloys obey the relationship: lambda(2).v = C, where lambda is the eutectic spacing, v is a tip growth rate and C is a constant. The aim of this study is to establish correlations between lambda and v for hypoeutectic Al-1%, 3% and 5% Ni alloys. Unsteady-state upward directional solidification experiments were performed, as well as metallography, dissolution of the aluminum matrix and scanning electron microscopy (SEM). The interphase spacing of the three Al-Ni alloys decreased with increasing tip growth rate, with a predominance of a rod-like morphology on intermetallic. It was observed that parameters such as tip growth rate, cooling rate and temperature gradient decreases as the solidification front advances. It was further observed that a single experimental law lambda = 1.2 v(-0.5) illustrates the evolution of the interphase spacing for any examined alloy.
Subject: Al-Ni alloys
unidirectional solidification
interphase spacing
Country: Brasil
Editor: Univ Fed Sao Carlos, Dept Engenharia Materials
Citation: Materials Research-ibero-american Journal Of Materials. Univ Fed Sao Carlos, Dept Engenharia Materials, v. 14, n. 2, n. 268, n. 273, 2011.
Rights: aberto
Identifier DOI: 10.1590/S1516-14392011005000034
Date Issue: 2011
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000292723200021.pdf2.2 MBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.