Title: Modulated photoactivation methods: Influence on contraction stress, degree of conversion and push-out bond strength of composite restoratives
Author: Cunha, LG
Alonso, RCB
Pfeifer, CSC
Correr-Sobrinho, L
Ferracane, JL
Sinhoreti, MAC
Abstract: Objectives: Verify the influence of curing methods on contraction stress, stress rate, and degree of conversion (DC) of a restorative composite and on bond strength of composite restoratives. Methods: For the stress test, composite (0.84 mm thick) was applied between two 5-mm diameter glass rods, mounted in a servohydraulic machine. Stress rate was taken by the value of stress/time at each second. DC was measured by micro-FTIR. Bond strength testing was performed using a push-out test. The C-factor in all tests was 3.0. Four curing methods were tested: continuous light (CL), soft-start (SS), and two pulse delay methods using different initial irradiances-150 mW/cm(2) (PD150) and 80 mW/cm(2) (PD80). Results were analyzed by ANOVA and Tukey's test (alpha = 0.05). Results: Stress values ranged from 7.9 MPa (PD80) to 10.3 MPa (CL). No statistical difference was verified among CL, SS, and PD150. PD80 presented statistically lower stress values compared to CL and SS. CL presented the highest maximum stress rate, followed by SS, PD150 and PD80. Mean DC values ranged from 54.2% (PD150) to 55.9% (PD80), with no difference observed among the methods. For the bond strength test, values ranged from 26.4 MPa (CL) to 35.5 MPa (PD150). PD150 and PD80 were both statistically superior to SS and CL. SS presented statistically higher bond strength compared to CL. Conclusions: Modulated curing methods were shown to be effective in reducing contraction stress rate and improving the strength of the bonded interface, and without compromising the DC of the restorative composite. (c) 2006 Elsevier Ltd. All rights reserved.
Subject: curing methods
restorative composite
FTIR contraction stress
bond strength
composite restoratives
Country: Inglaterra
Editor: Elsevier Sci Ltd
Citation: Journal Of Dentistry. Elsevier Sci Ltd, v. 35, n. 4, n. 318, n. 324, 2007.
Rights: fechado
Identifier DOI: 10.1016/j.jdent.2006.10.003
Date Issue: 2007
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000245565300007.pdf404.23 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.