Title: Recuperação de níquel por eletrodeposição para formação de ligas com tungstênio e cobalto : Nickel recovery by electrodeposition to formate alloys with tungsten and cobalt
Title Alternative: Nickel recovery by electrodeposition to formate alloys with tungsten and cobalt
Author: Portela, Daniella Gonçalves, 1993-
Advisor: Almeida Neto, Ambrósio Florêncio de, 1979-
Abstract: Resumo: A procura por inovações tecnológicas para suprir as necessidades de uma produção eficiente e limpa motivam o desenvolvimento de pesquisas como a remoção de metais tóxicos de efluentes e o aperfeiçoamento de materiais com boa durabilidade e resistente a corrosão. Neste trabalho promoveu-se a síntese de ligas ternárias a partir de um planejamento feito com banho sintético e um com efluente contendo níquel para reciclar uma parte desse níquel e obter um material com propriedades anticorrosivas. Os resultados das eletrodeposições das ligas obtidas com a remoção do níquel e por reagentes sintéticos puros foram avaliados considerando a capacidade de recuperação do níquel da fase líquida, a eficiência de deposição e o desempenho dessas ligas em um meio corrosivo para revestimento industrial em diferentes condições físico-químicas. Os métodos de caracterização utilizados nas ligas obtidas serão: Difração de Raios X (DRX) e Microscopia Eletrônica de Varredura com Análise Química por Energia Dispersiva de Raios X (EDX), para analisar a cristalinidade, a homogeneidade, a composição e a distribuição dos constituintes da liga. Com a caracterização das ligas foi observado que o diferença de potencial durante a eletrodeposição se manteve constante e resultou em deposição preferencial dos grãos, formando revestimentos com composições parecidas, independente dos parâmetros. Todas as ligas foram policristalinas com uma fase homogênea das estruturas cúbica de face centrada e hexagonal compacta. A partir do banho sintético foram utilizados valores de parâmetros que tiveram características morfológicas e cristalinas ao do banho sintético, porém com maior eficiência em um menor tempo de eletrodeposição. O percentual de remoção de níquel do efluente foi de apenas 12%, indicando a baixa eficácia de remoção, porém observou-se uma relação entre aumento de remoção para temperaturas maiores. As ligas de maior eficiência catódica se tornam resistentes à corrosão (159 k?.cm²), quando comparadas a outros resultados da literatura do Ni-Co-W. Nas ligas depositadas a partir do efluente a resistência a corrosão foi propiciada nos depósitos com maior quantidade de massa por unidade de área. Como principal resultado desse trabalho foi obtida uma liga de Ni-Co-W, produzida a partir de uma efluente, com eficiência catódica de 86,89%, densidade de corrente de corrosão de 0,489 ?A/cm² e potencial de corrosão de - 160,46 V

Abstract: The research for technological innovations to supply necessities of efficient and clean production motivates studies development such as the removal of toxic metals from effluents and new materials with good durability. In this study, the ternary alloys were produced from baths with synthetic reagents and with effluent nickel to recycle nickel from effluent and obtain a material resistant to corrosion. The electrodeposited alloys obtained with nickel removal and by pure synthetic reagents were evaluated considering the nickel recovery capacity of the liquid phase, the current efficiency and the performance of these alloys in a corrosive medium for industrial coating in different physical-chemicals conditions. The X-ray diffraction (XRD) and Scanning Electron Microscopy with X-ray Dispersive Energy (EDX) chemical analysis methods were used to analyze the crystallinity, homogeneity, composition and compounds distribution in the alloy. With the coatings characterization it was observed that overpotential was maintained constant and resulted in grains preferential deposition, forming coatings with similar compositions, independent of parameters. All the alloys were polycrystalline with cubic face centered (cfc) and hexagonal close-packed (hcp) structures homogeneous phase. In the baths with effluent were obtained deposits with morphological and crystalline characteristics similar to the synthetic bath, however they presented greater efficiency and were evaluated in a shorter electrodeposition time. The nickel removal percentage from effluent was 12%, indicating low removal efficiency, however, a relationship between increased removal at higher temperatures was observed. The higher cathodic efficiency alloys become resistant to corrosion (159 k?.cm²) when compared to other results for Ni-Co-W found in literature. In the alloys obtained through effluent bath, the corrosion resistance was favored in deposits with more mass per unit of area. The main result of this work was a Ni-Co-W alloy produced from an effluent, with 86.89% of cathodic efficiency, 0.489 ?A/cm² of corrosion current density and corrosion potential of -0.16046 V
Subject: Efluentes
Ligas metálicas
Corrosão e anticorrosivos
Language: Português
Editor: [s.n.]
Citation: PORTELA, Daniella Gonçalves. Recuperação de níquel por eletrodeposição para formação de ligas com tungstênio e cobalto: Nickel recovery by electrodeposition to formate alloys with tungsten and cobalt. 2019. 1 recurso online (93 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química, Campinas, SP.
Date Issue: 2019
Appears in Collections:FEQ - Tese e Dissertação

Files in This Item:
File SizeFormat 
Portela_DaniellaGoncalves_M.pdf4.9 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.