Type: DISSERTAÇÃO DIGITAL
Degree Level: Mestrado
Title: Avaliação das propriedades físicas e antibacterianas de infiltrantes experimentais contendo sal de iodônio e quitosana
Title Alternative: Evaluation of the physical and antibacterial properties of experimental infiltrants containing iodonium salt and chitosan
Author: Ribeiro, Mariana Dias Flor, 1991-
Advisor: Marchi, Giselle Maria, 1970-
Abstract: Resumo: Lesões de mancha branca ocorrem devido à desmineralização inicial do esmalte, o que leva a formação de porosidades no interior desse substrato. Na tentativa de impedir a progressão da lesão, foram desenvolvidos infiltrantes - materiais resinosos de baixa viscosidade ¿ os quais atuam preservando a forma anatômica dos dentes por infiltrarem em profundidade na superfície da lesão de cárie incipiente. O objetivo do presente estudo foi analisar as propriedades físicas e antibacterianas de infiltrantes experimentais contendo sal de iodônio e quitosana. Para isso, nove infiltrantes experimentais contendo a base monomérica de trietilenoglicol dimetacrilato (TEGDMA) e bisfenol-A dimetacrilato etoxilato (BisEMA) em proporção de 75 e 25% em peso, respectivamente; 0,5 mol% de canforoquinona (CQ) e 1 mol% de 4-dimetilaminobenzoato de etila (EDAB) como sistema fotoiniciador foram formulados variando a concentração do sal de iodônio (DFI) em 0; 0,5 e 1 mol% e de quitosana em 0; 0,12 e 0,25 g%. Os compostos foram preparados em ambiente com controle de iluminação, temperatura e umidade. Foram avaliados o grau de conversão usando a espectroscopia de infravermelho com transformador de Fourier, resistência à flexão e módulo de elasticidade pelo teste de flexão de três pontos, sorção e solubilidade em água e análise antibacteriana (Concentração Inibitória Mínima - CIM - e Concentração Bactericida Mínima - CBM). Os dados foram analisados estatisticamente por Análise de Variância a dois critérios (ANOVA) e teste de Tukey (p<0,05), com exceção do teste antibacteriano, que foi avaliado pelo método de inspeção visual. Em geral, o grupo de infiltrante contendo 0,5% de DFI e 0,12% de quitosana apresentou altos valores de grau de conversão, maiores valores de módulo de elasticidade e resistência à flexão e menores valores de sorção de água em relação aos demais grupos. Atividade antibacteriana foi constatada em todos os grupos com DFI, independentemente da concentração de quitosana envolvida. Conclui-se que a adição de sal de iodônio e quitosana à infiltrantes experimentais constituem alternativas viáveis para a melhoria de suas propriedades mecânicas e antibacterianas

Abstract: White spot lesions ocurr due to the initial demineralization of the enamel, which leads to the formation of porosities inside this tissue. In order to prevent the progression of the lesion, the development of infiltrants - resinous materials of low viscosity - has occurred, which act to preserve the anatomical shape of the teeth by infiltrating deep into the surface of the incipient caries lesion. The aim of the present study was to analyze the phisical and antibacterial properties of experimental infiltrants containing iodonium salt and chitosan in their formulation. For this, nine experimental infiltrants containing the monomeric base triethylene glycol dimethacrilate (TEGDMA) and bisphenol A ethoxylated dimethacrylate (BisEMA) in the proportion 75 and 25% by weight, respectively; 0,5 mol% of camphorquinone (CQ) and 1 mol% of ethyl 4-(dimetilamino)benzoate (EDAB) as a photoinitiator system were formulated by varying the concentration of iodonium salt (DFI) at 0; 0,5 and 1mol% and chitosan at 0; 0,12 and 0,25 wt%. The compounds were formulated in ambient light, temperature and humidity control. The degree of conversion using Fourier transformer infrared spectroscopy, flexural strength and modulus of elasticity by three-point flexural test, water sorption and solubility and antibacterial analysis (Minimum Inhibitory Concentration ¿ MIC and Minimum Bactericidal Concentration - MBC) were evaluated. Data were analyzed statistically by two-way ANOVA and Tukey's test (p<0,05), except for the antibacterial test, which was evaluated by the visual inspection method. In general, infiltrant group containing 0,5% DFI and 0,12% chitosan presented high values of conversion degree, higher values of modulus of elasticity and flexural strength, and lower values of water sorption in relation to the others groups. Antibacterial activity was observed in all groups with DFI, independent of the concentration of chitosan involved. It is concluded that the addition of ion and chitosan salt to the experimental infiltrants are viable alternatives for the improvement of their mechanical and antibacterial properties
Subject: Resinas compostas
Oniocompostos
Quitosana
Editor: [s.n.]
Citation: RIBEIRO, Mariana Dias Flor. Avaliação das propriedades físicas e antibacterianas de infiltrantes experimentais contendo sal de iodônio e quitosana. 2017. 1 recurso online (56 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/331395>. Acesso em: 1 set. 2018.
Date Issue: 2017
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Ribeiro_MarianaDiasFlor_M.pdf1.63 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.