Title: Scaffolds derivados do biovidro 58S contendo íons Na : síntese por sol-gel e modificação de superfície para liberação de óxido nítrico
Title Alternative: Scaffolds derived from 58S bioglass containing Na ions : sol-gel synthesis and surface modification for nitric oxide release
Author: Gomes, Paula, 1991-
Advisor: Bertran, Celso Aparecido, 1951-
Abstract: Resumo: Os biovidros têm se mostrado bastante promissores como implantes ósseos, por causa de suas propriedades bioativas. Nesta dissertação, foi desenvolvido um biovidro que apresentou composição semelhante a do biovidro 58S com adição de íons Na+, denominado 58S3N neste trabalho. Para que o material apresentasse uma estrutura porosa, típica de scaffolds, foi empregada a rota de síntese por sol-gel acoplada ao método ISISA (ice-segregation-induced self-assembly), que levou à formação de um material com poros interconectados de até 50 µm. Para se obter um biovidro poroso e com resistência mecânica adequada, o biovidro 58S3N foi calcinado a 600°C por um período de 5 min sem rampa de aquecimento, permitindo que ele apresentasse resistência ao manuseio e, ao mesmo tempo, preservasse os grupos silanois (Si ¿OH) superficiais. A presença dos grupos ¿Si-OH permitiu a modificação da superfície do biovidro com S-nitrosoglutationa (GSNO) que libera óxido nítrico (NO) para aumentar a bioatividade do material e diminuir a possibilidade de reações infecciosas. O material poroso modificado foi analisado em condições semelhantes às encontradas em implantes ósseos e mostrou uma liberação controlada de NO para o meio por um período de mais de 7 h. Para verificar o comportamento bioativo do biovidro 58S3N funcionalizado para liberação de NO, ensaios in vitro foram realizados. Esses ensaios mostraram a formação de fosfato de cálcio sobre a superfície do material, que é essencial para o reconhecimento das células ósseas, e a ausência de processos inflamatórios quando o biovidro é implantado

Abstract: Bioglasses have been shown to be quite promising as bone implants because of their bioactive properties. In this dissertation, a bioglass with addition of Na+ ions, possessing a composition similar to that of 58S bioglass was developed and named 58S3N. In order to obtain a porous structure, typical of scaffolds the Ice-segregation-induced self-assembly (ISISA) method was used, which led to the formation of a material with interconnected pores of up to 50 ?m. To obtain a porous bioglass with adequate mechanical strength, the 58S3N bioglass was calcined at 600°C for a period of 5 min without heating ramp, allowing it to exhibit resistance to handling and at the same time preserving the silane groups (Si -OH). The presence of Si-OH groups allowed the modification of the bioglass surface with nitric oxide (NO)-releasing S-nitrosoglutathione (GSNO), in order to increase the bioactivity of the material and reduce the possibility of infectious reactions. The modified porous material was analyzed under conditions similar to those found in bone implants and showed a controlled release of NO to the medium for a period of more than 7 h. To verify the bioactive behavior of the 58S3N biofunctional bioglass for NO release, in vitro assays were performed. These assays showed the formation of calcium phosphate on the surface of the material, which is essential for the recognition of bone cells and the absence of inflammatory processes when bioglass is implanted
Subject: Biovidro 58S
Óxido nítrico
Language: Português
Editor: [s.n.]
Citation: GOMES, Paula. Scaffolds derivados do biovidro 58S contendo íons Na: síntese por sol-gel e modificação de superfície para liberação de óxido nítrico. 2017. 1 recurso online (98 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Química, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/330919>. Acesso em: 3 set. 2018.
Date Issue: 2017
Appears in Collections:IQ - Tese e Dissertação

Files in This Item:
File SizeFormat 
Gomes_Paula_M.pdf3.51 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.