Degree Level: Mestrado
Title: Influência da aplicação de plasma de argônio não térmico nas propriedades mecânicas e transformação de fase da zircônia Y-TZP = Influence of non-thermal argon plasma on the mechanical properties and phase transformation of Y-TZP zirconia
Title Alternative: Influence of non-thermal argon plasma on the mechanical properties and phase transformation of Y-TZP zirconia
Author: Negreiros, William Matthew, 1992-
Advisor: Giannini, Marcelo, 1969-
Abstract: Resumo: O objetivo deste estudo foi avaliar a influência de diferentes tempos de aplicação de plasma de argônio frio (NTP) e do envelhecimento acelerado em autoclave na resistência flexural, módulo de elasticidade, conteúdo cristalino e caracterização da topografia de uma zircônia tetragonal policristalina (Y-TZP, ZirCAD, Ivoclar Vivadent). O NTP foi aplicado na zircônia por 0, 10 e 60 segundos. Para as análises da resistência flexural e módulo de elasticidade (teste de 4 pontos e velocidade de 1mm/min) foram preparados espécimes com dimensões de 45 mm de comprimento, 4.0 mm de largura e 3.0 mm de espessura (n = 10) e o envelhecimento artificial em autoclave realizado por 0 (baseline), 4 e 30 horas. Os dados foram analisados estatisticamente pela análise de variância 2 fatores e teste de Tukey (?=5%). Para caracterização do conteúdo cristalino (volume monoclínico) da zircônia em função do tempo de envelhecimento e tratamento com NTP, um espécime por grupo foi submetido à análise por difração de raios-x (XRD) nos tempos de envelhecimento de: 0, 2, 4, 6, 8, 10, 15, 20 e 30 horas. A análise topográfica do material foi realizada em microscopia de força atômica no modo "sem contato" utilizando os mesmos espécimes avaliados em XRD. Os resultados mostram que não houve interação entre tipo de tratamento e tempo de envelhecimento em autoclave para os resultados de deflexão e módulo (p>0.05). O tempo de 30 horas de envelhecimento em autoclave resultou em aumento estatisticamente significativo dos resultados de resistência flexural quando comparado ao baseline para o grupo controle (p<0.05). Com relação ao módulo de elasticidades o tempo de 30 horas de envelhecimento produziu aumento significativo quando comparado ao baseline e 4 horas para todos os tratamentos (p<0.05). O conteúdo monoclínico tendeu aumentar com o envelhecimento artificial da zircônia. Não foi observada nenhuma alteração nas superfícies da zircônia independente do tratamento e tempo de envelhecimento. A aplicação de NTP mostrou não afetar negativamente as propriedades mecânicas da Y-TZP testada. O volume monoclínico aumentou em função do tempo em autoclave, sendo levemente maior nos espécimes tratados com NTP. O envelhecimento modifica o arranjo cristalino da Y-TZP e juntamente com o NTP não alteraram a topografia de superfície da mesma

Abstract: The objective of this study was to evaluate the influence of different times of non-thermal plasma (NTP) application and the accelerated aging in autoclave on flexural strength, elastic modulus, crystalline content and topography characterization of an Yttrium-stabilized Tetragonal Zirconia Polycrystal (Y-TZP, ZirCAD, Ivoclar Vivadent). The NTP was applied onto the zirconia surface for 0, 10 and 60 seconds. For flexural strength and modulus (4-point bending test at a crosshead speed of 1 mm/min) specimens with dimensions of 45 mm in length, 4.0 mm in width and 3.0 mm in thickness were prepared (n=10) and the accelerated aging in autoclave was conducted for 0 (baseline), 4 and 30 hours. Data were analyzed by 2-way ANOVA and post-hoc Tukey test (?=5%). To analyze the crystalline content of the zirconia specimens (monoclinic volume) in function of NTP treatment and aging, one specimen from each group was submitted to X-Ray Diffraction (XRD) after the following aging periods: 0, 2, 4, 6, 8, 10, 15, 20 and 30 hours. Topographic analysis of the same specimens submitted to XRD was performed with atomic force microscopy (AFM) in "non-contact" mode. Results show no interaction between type of treatment and aging time in autoclave for flexural strength and modulus (p>0.05). At 30 hours of aging in autoclave, there was a statistically significant increase in the flexural strength when compared to baseline in the control group (p<0.05). At 30 hours of aging, elastic modulus showed a statistically significant increase when compared to baseline and 4 hours for all types of treatment (p<0.05). Monoclinic content tended to increase following the zirconia aging. No change in zirconia surfaces was observed regardless of treatment and aging time. NTP application did not negatively affect the mechanical properties of the tested Y-TZP. Monoclinic volume increased as a function of time in autoclave, being slightly higher in NTP treated specimens. Aging modifies the crystalline phase of Y-TZP and, along with NTP, it does not alter surface topography
Subject: Zirconio
Resistência de materiais
Módulo de Elasticidade
Transição de fase
Language: Multilíngua
Editor: [s.n.]
Citation: NEGREIROS, William Matthew. Influência da aplicação de plasma de argônio não térmico nas propriedades mecânicas e transformação de fase da zircônia Y-TZP = Influence of non-thermal argon plasma on the mechanical properties and phase transformation of Y-TZP zirconia. 2017. 1 recurso online (39 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/322020>. Acesso em: 1 set. 2018.
Date Issue: 2017
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Negreiros_WilliamMatthew_M.pdf2.25 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.