Title: Diferenciação de células-tronco embrionárias em cardiomiócitos sobre diferentes substratos poliméricos
Title Alternative: Differentiation of embryonic stem cells into cardiomyocytes over different polymeric substrates
Author: Melo, Vinicius André Morais Rocha, 1983-
Advisor: Duek, Eliana Aparecida de Rezende, 1961-
Abstract: Resumo: A ciência dos biomateriais é uma área de conhecimento multidisciplinar e amplamente utilizada para recuperar e/ou restaurar a função de um órgão danificado. Dentre as aplicações atuais dos biomateriais, a utilização de polímeros biorreabsorvíveis como arcabouço para cultura de células tem se destacado como uma terapia alternativa no tratamento de lesões e perda de tecidos como a que ocorre durante o infarto do miocárdio. Células-tronco Embrionárias (ESCs) oferecem um grande potencial terapêutico para o tecido cardíaco. Neste estudo, foi avaliado a interação das ESCs com o poli L-co-D,L ácido lático-co-trimetileno carbonato (PLDLA-co-TMC) e o Hidrogel de poli(NIPAAm-co-AAc-co-HEMAPLDLA-co-TMC) na diferenciação de células-tronco embrionárias de camundongos (mESC) em cardiomiócitos por qPCR e Imunofluorescência, assim como, a caracterização destes materiais por meio das técnicas de MEV, DSC, GPC, TGA, Ensaio Mecânico de Tração e Ensaio de Toxicidade. Através dos resultados obtidos, foi verificado que, as unidades de TMC adicionadas ao PLDLA influenciaram nas propriedades do material, proporcionando maior flexibilidade ao biopolímero. O PLDLA-co-TMC apresentou perda de massa, acompanhada da redução das propriedades mecânicas ao longo do processo de degradação hidrolítica. Enquanto o Hidrogel se apresentou como um material injetável com baixo tempo de gelificação e sua caracterização térmica por DSC evidenciou o comportamento típico dos hidrogéis: LCST (temperatura de transformação de fase), responsável pelas características termossensíveis do material. Os ensaios de cultivo e diferenciação de mESC em cardiomiócitos sobre o Hidrogel e as membranas de PLDLA-co-TMC, que representam o principal objetivo deste trabalho, asseguraram a citocompatibilidade destes polímeros, além de evidenciarem que não apresentam toxicidade às células onde foram cultivadas pois permitiram a adesão e proliferação das células-tronco, assim como, a diferenciação das células-tronco embrionárias de camundongo em cardiomiócitos, sugerindo que ambos os polímeros são aceitáveis para terapia regenerativa cardíaca sendo recomendados para o uso na engenharia tecidual

Abstract: The biomaterial science is a multidisciplinary field of knowledge and widely used to recover and/or restore the function of a damaged organ. Among the current biomaterial applications, the use of bioabsorbable polymers as cell scaffold has been considered as an alternative therapy in the treatment of injuries and tissue loss, such as during myocardial infarct. Embryonic stem cells (ESC) provide a great therapeutic potential for cardiac tissue. In this study, was assessed the mESC interaction with the poly L-co-D,L lactic acid-co-trimethylene carbonate (PLDLA-co-TMC) and the Hydrogel of poly(NIPAAm-co-AAc-co-HEMAPLDLA-co-TMC), in the differentiation of mouse embryonic stem cells (mESC) into cardiomyocytes throughout qPCR and Immunofluorescence analysis, as well as the characterization of these materials by means of SEM, DSC, GPC, TGA, Tensile Mechanical Test and Toxicity Test techniques. From the obtained results, it was verified that the TMC elements added to PLDLA influenced the material proprieties, providing greater flexibility to the biopolymer. The scaffolds showed weight loss, accompanied by the reduction of mechanical proprieties throughout the hydrolytic degradation process. Meanwhile, the Hydrogel showed itself as an injectable material with low jellification time and its thermal characterization by DSC showed the typical behavior of hydrogels: LCST (Lower Critical Solution Temperature), accountable for the thermoresponsive characteristic of the material. The cell growth and mESC differentiation assays into Hydrogel and membranes of PLDLA-co-TMC, which represent the main objective of this study, ensure cytocompatibility of these polymers, also evidence that they show no toxicity to the cells which they were grown, allowing adhesion and cell proliferation, as well as the embryonic stem cell differentiation into cardiomyocytes, suggesting that both polymers are acceptable for regenerative cardiac therapy and recommended for use in tissue engineering
Subject: Polímeros
Hidrogel
Células-tronco embrionárias
Regeneração tecidual guiada
Editor: [s.n.]
Citation: MELO, Vinicius André Morais Rocha. Diferenciação de células-tronco embrionárias em cardiomiócitos sobre diferentes substratos poliméricos. 2015. 1 recurso online ([17]94 p.). Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/265731>. Acesso em: 28 ago. 2018.
Date Issue: 2015
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Melo_ViniciusAndreMoraisRocha_D.pdf15.03 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.