Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/264971
Type: DISSERTAÇÃO
Degree Level: Mestrado
Title: Uma metodologia para a avaliação dos gradientes de tenacidade a fratura ao longo da camada cementada do aço SAE 5115
Title Alternative: A model for fracture toughness evaluation of the carburized layer for SAE 5115 steel
Author: Sandor, Leonardo Taborda
Advisor: Ferreira, Itamar, 1952-
Abstract: Resumo: Este trabalho propõe um modelo para avaliar pontualmente as variações de tenacidade à fratura ao longo da camada cementada de um aço SAE 5115. A pequena espessura dessas camadas impede a retirada de corpos de prova nas dimensões especificadas pelas normas de ensaios de tenacidade à fratura. Assim, para simular uma camada cementada retirou-se corpos de prova de tração e de tenacidade à fratura de amostras de aços SAE 5115, 5140, 5160 e 52100 assumindo a influência local apenas da variação do teor de carbono e considerando que os teores dos demais elementos de liga são essencialmente constantes. Os corpos de prova após eletrodeposição de cobre foram tratados termicamente numa carga industrial de cementação, têmpera e revenimento para serem submetidos aos efeitos térmicos sem absorção de carbono. Os resultados da análise microestrutural, dos ensaios de microdureza, de tração e de tenacidade à fratura foram agrupados em um único gráfico e comparados com o perfil de cementação de peças de aço SAE 5115 tratadas nas mesmas condições. Foi confirmado que a tenacidade à fratura varia inversamente proporcional à microdureza (HV1) e que a previsão do comportamento de uma trinca numa camada cementada pode ser feita por meio de equação ou diagrama que relacionam a miicrodureza HV1 com a tenacidade à fratura (K1c ou CTODc)

Abstract: The purpose of this work is to propose a model for evaluating the fracture toughness along the SAE 5115 steel carburized layer. Due to the small thickness of those layers, it is impossible to machine specimens from those layer in accordance with standards. For simulating the microstructures of the carburized layer in order to get samples for tensile and the fracture toughness testing, specimens of SAE 5115, 5140, 5160, and 52100 steels assuming the local influence just of the variation of the content of carbon and considering that the contents of the other alloy elements are essentially constant. The specimens after electroplated copper layer were heat treated in an industrialload of carburizing, quenching, and tempering for they be submitted to the thermal effects without absorption of carbono The results of the microstructure analysis and microhardness, tension, and fracture toughness tests were placed in a single graph and compared with the profile of the carburizing of the steel SAE 5115 heat treated in the same conditions. It was confirmed that the fracture toughness varies inversely proportional to the microhardness (HV1) and that the forecast of the behavior of a crack in a carburized layer can be made through equation or it designs that relate the microhardness (HV1) with the fracture toughness (KIC or CTODc)
Subject: Mecânica da fratura
Fractografia
Metalografia
Aço - Fadiga
Processo de endurecimento superficial
Aço de alta resistencia
Language: Português
Editor: [s.n.]
Citation: SANDOR, Leonardo Taborda. Uma metodologia para a avaliação dos gradientes de tenacidade a fratura ao longo da camada cementada do aço SAE 5115. 2005. 153p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica, Campinas, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/264971>. Acesso em: 4 ago. 2018.
Date Issue: 2005
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
Sandor_LeonardoTaborda_M.pdf9.41 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.